Optical Microscope

2 cases · 7 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: 10222-5 Detail focus: Heat Affected Zone clear all

Optical Microscope — sub-branches

Kalling Etched Micrography by OM 3NaOH Electrolytic Etched Micro 4

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic detail of the heat-affected zone close to the base metal.
29
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched Micrography by OMDf - Heat Affected Zone
Micrography of the pipe heat affected zone. In the left the pipe base metal, with banded duplex structure; and in the right the weld metal, with Widmanstatten morphology of the structure.
43
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MicroDf - Heat Affected Zone

More from these cases

ML00045 — Subsea Tubular F6NM Martensitic SSM - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Micrographic detail of the heat-affected zone close to the fusion line.
31
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched Micrography by OMDf - Heat Affected Zone
Micrography of the heat-affected zone. The fusion line is in the right and the coarse structure of the base metal is refined at the heat affected zone.
28
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched Micrography by OMDf - Heat Affected Zone
ML00049 — Pipe to Flange Welded Joint in a 14" ND Superduplex SpoolM - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Higher magnification of the pipe heat affected zone. The amount of ferrite increases with the proximity of the fusion line (to the right).
38
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MicroDf - Heat Affected Zone
Micrography of the flange heat affected zone. In the right the flange base metal, with coarse structure and detrimental phases associated to the ferrite; and in the left the weld metal, with Widmanstatten morphology of the structure.
36
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MicroDf - Heat Affected Zone
Higher magnification of the flange heat affected zone. The detrimental phases in the ferrite structure is clearly being dissolved with the proximity of the fusion line (to the left).
28
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MicroDf - Heat Affected Zone