Optical Microscope

2 cases · 8 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Martensite Standard: API Detail focus: Damage clear all

Optical Microscope — sub-branches

Micrography by OM 2Nital Etched Micrography by OM 6

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic detail of a longitudinal section of the pin, at the fracture position, showing secondary cracks with intergranular and transgranular morphology.
59
VIEW
ML00009 / Sep.2017
Hydrogen Cracking of a 5" Drill Pipe S135
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Brittle Cracks
The micrography in the as polished condition of the longitudinal section of the pipe close to the washout, shows that at the tool mark tip (notch from the external surface) a fatigue crack already started from a corroded region (pitting).
187
VIEW
ML00068 / Sep.2020
Corrosion Fatigue of a 5" Drill Pipe
M - Low Alloy Medium Carbon QTP - Seamless PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Micrography by OMDf - Pitting

More from these cases

ML00009 — Hydrogen Cracking of a 5" Drill Pipe S135M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Micrography of a longitudinal section of the pin, at the fracture position, showing a low magnification aspect of the fracture surface (top of the figure) and secondary cracks associated to the segregation band.
51
VIEW
ML00009 / Sep.2017
Hydrogen Cracking of a 5" Drill Pipe S135
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Cracking
Micrography of a longitudinal section of the pin, at the fracture position, showing the main fracture surface and secondary cracks associated to a segregation band, with an intergranular morphology.
49
VIEW
ML00009 / Sep.2017
Hydrogen Cracking of a 5" Drill Pipe S135
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Intergranular Cracking
Micrographic detail of a longitudinal section of the pin, at the fracture position, showing secondary cracks with intergranular morphology.
48
VIEW
ML00009 / Sep.2017
Hydrogen Cracking of a 5" Drill Pipe S135
M - Low Alloy Medium Carbon QTP - Drill PipeAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Secondary Cracks
ML00068 — Corrosion Fatigue of a 5" Drill PipeM - Low Alloy Medium Carbon QTP - Seamless PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Micrographic detail, in the as polished condition, of the corrosion fatigue crack.
90
VIEW
ML00068 / Sep.2020
Corrosion Fatigue of a 5" Drill Pipe
M - Low Alloy Medium Carbon QTP - Seamless PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Micrography by OMDf - Fatigue Crack
The micrography of one of the (multiple) cracks shows the slightly irregular morphology of the cracking, typical of a corrosion-fatigue mechanism.
281
VIEW
ML00068 / Sep.2020
Corrosion Fatigue of a 5" Drill Pipe
M - Low Alloy Medium Carbon QTP - Seamless PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Corrosion Cracking
Micrographic detail of the slightly irregular crack propagation, typical of a corrosion-fatigue mechanism.
76
VIEW
ML00068 / Sep.2020
Corrosion Fatigue of a 5" Drill Pipe
M - Low Alloy Medium Carbon QTP - Seamless PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Nital Etched Micrography by OMDf - Corrosion Cracking