Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Graphite in nodules Detail focus: Damage clear all

Optical Microscope — sub-branches

Nital Etched Micrography by OM 4

Results

SortNewestOldestTitle A-ZTitle Z-A
The micrography of the stem at the fracture region shows a flat fracture with transgranular clevage at the ferritic structure.
137
VIEW
ML00040 / Apr.2017
Brittle Fracture of a Valve Stem
M - Nodular Cast IronP - Valve StemAp - ShipCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Fracture
Polished cross-section showing rounded graphite nodules within a ferritic matrix, bordered by an irregular oxidized region at the surface edge.
910
VIEW
ML00001 / Dec.2017
Thermal Fatigue of Cast Iron
M - Nodular Cast IronP - CastAp - SiderurgyCd - Thermal Fatigue
Cm - Nital Etched Micrography by OMDf - Oxide Layer

More from these cases

ML00040 — Brittle Fracture of a Valve StemM - Nodular Cast IronP - Valve StemAp - ShipCd - Brittle Fracture
Micrography presenting a detail of the fracture surface opening to the graphite nodules.
139
VIEW
ML00040 / Apr.2017
Brittle Fracture of a Valve Stem
M - Nodular Cast IronP - Valve StemAp - ShipCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Fracture
ML00001 — Thermal Fatigue of Cast IronM - Nodular Cast IronP - CastAp - SiderurgyCd - Thermal Fatigue
The graphite nodules remain at the surface and the matrix was consumed during high temperature exposition.
117
VIEW
ML00001 / Dec.2017
Thermal Fatigue of Cast Iron
M - Nodular Cast IronP - CastAp - SiderurgyCd - Thermal Fatigue
Cm - Nital Etched Micrography by OMDf - Oxide Layer