Optical Microscope

9 cases · 11 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Fabrication Defect Detail focus: Martensite clear all

Optical Microscope — sub-branches

Kalling Etched Micrography by OM 2Nital Etched Micrography by OM 9

Results

SortNewestOldestTitle A-ZTitle Z-A
Grain coarsened martensitic heat affected zone. The hardness values about 270HV10 indicates that the joint was post welding heat treated (PWHT).
97
VIEW
ML00178 / Jan.2022
Cold cracks in Cr-Mo Welded Forging
M - CrMo SteelP - ForgingAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Martensite
Micrographic detail of the nut longitudinal section presenting the large carbides (white islands) in the segregation band, and small precipitates all through the martensite matrix, indicating that this high carbon steel was tempered in a high temperature. The 36HRc hardness also confirms this high tempering temperature.
39
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Martensite
Micrographic detail of the roller bearing microstructure, close to the external surface, presenting 64 HRc and a microstructure that is martensitic with large carbides.
86
VIEW
ML00131 / Apr.2018
Brittle Failure of a Soft Roller Bearing
M - Wear Resistant SteelP - Roller BearingAp - Mechanical IndustryCd - Heat Treatment Defect
Cm - Nital Etched Micrography by OMDf - Martensite
Micrography of the shaft at the surface, in a region where a thermal spray layer was not applied. The microstructure at the shaft surface is martensitic (low carbon martensite) typical of a quenched and tempered condition for this low alloy steel. The heat treatment was probably conducted before the thermal spray layer was applied.
24
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - Nital Etched Micrography by OMDf - Martensite
Tempered martensitic microstructure in the transverse section of the nut, in the center. The material presented 29 HRc that is typical of a quenched and tempered steel.
30
VIEW
ML00099 / Jan.2018
Forging Defect in a Cadmium Plated Nut
M - Medium Carbon SteelP - NutAp - PipingCd - Fabrication Defect
Cm - Nital Etched Micrography by OMDf - Martensite
Micrographic detail of the AISI 4130 forging, 5/8" thickness, close to the welded region, in the longitudinal section. Bainitic and tempered martensitic structure.
47
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Martensite
Micrography of the weld metal in a cracked region. Non tempered martensitic regions. This part is not typically stress relieved after welding.
50
VIEW
ML00067 / May.2017
Cold Cracks in C-Mn SAW Weld Metal
M - CMn SteelP - Fabrication WeldAp - AutomotiveCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Martensite
The micrography shows the martensitic region of the tube HAZ responsible for the hydrogen cracking, presenting too high hardness level (600 HV). It is a fresh martensite since the joint was welded in one pass and there was no PWHT.
45
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Martensite

More from these cases

ML00131 — Brittle Failure of a Soft Roller BearingM - Wear Resistant SteelP - Roller BearingAp - Mechanical IndustryCd - Heat Treatment Defect
Martensitic structure close to the external diameter of the cylindrical roller bearing, in the circuferemtial direction, presenting large carbides (not aligned due to the direction of the section) and a martensitic matrix. in this region the fracture presented quasecleavage micromechanism as well as decohesion of large carbides.
36
VIEW
ML00131 / Apr.2018
Brittle Failure of a Soft Roller Bearing
M - Wear Resistant SteelP - Roller BearingAp - Mechanical IndustryCd - Heat Treatment Defect
Cm - Nital Etched Micrography by OMDf - Martensite
ML00108 — Thermal Spray Layer in a Pinion ShaftM - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Micrographic detail of the shaft at the surface, in a region where a thermal spray layer was not applied. The microstructure is martensitic (low carbon martensite) typical of a quenched and tempered condition for this low alloy steel. The heat treatment was probably conducted before the thermal spray layer was applied.
29
VIEW
ML00108 / Dec.2017
Thermal Spray Layer in a Pinion Shaft
M - High Strength Low AlloyP - ShaftAp - EngineCd - Coating Defect
Cm - Nital Etched Micrography by OMDf - Martensite