Optical Microscope

2 cases · 4 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Damage Microstructure: Ferritic Bainitic Detail focus: Weld Metal clear all

Optical Microscope — sub-branches

Nital Etched Micrography by OM 4

Results

SortNewestOldestTitle A-ZTitle Z-A
WELD METAL T/2
28
VIEW
ML00177 / Dec.2021
Cr-Mo Seam Welded Tube
M - CrMo SteelP - Longitudinally Seam WeldedAp - Fired HeaterCd - Not according to spec
Cm - Nital Etched Micrography by OMDf - Weld Metal
The liquation crack is a hot crack in the base metal (at the HAZ) that induces a solidification crack in the weld metal.
66
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Weld Metal

More from these cases

ML00072 — Liquation Cracks in a High Strength JointM - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Micrography of the weld metal of the last bead. Columnar morphology and refined ferritic structure.
47
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Weld Metal
Micrographic detail of the weld metal of the last bead. Columnar morphology and refined ferritic structure.
57
VIEW
ML00072 / Jan.2018
Liquation Cracks in a High Strength Joint
M - Low Alloy Medium Carbon QTP - Longitudinal Seam Welded PipeAp - O&G Well DrillingCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Weld Metal