Optical Microscope

7 cases · 20 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Damage Standard: ASTM Detail focus: Cracks clear all

Optical Microscope — sub-branches

As polished micrography 4Kalling Etched Micrography by OM 2Micrography by OM using A262 Method A 1Nital Etched Micrography by OM 13

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic detail of the cracks in the base metal created from the partially melted region suggesting that a liquation effect propagated brittle cracks into the low ductility base metal.
30
VIEW
ML00173 / May.2021
Welding Cracks in an Aged HP Cast Fitting
M - Heat Resistant SteelP - Cast FtittingAp - PetrochemicalCd - Welding
Cm - Kalling Etched Micrography by OMDf - Cracks
Micrographic detail of the nut in the longitudinal section, presenting cracks associated to the plastic deformation at the thread surface. These cracks were formed due to high local contact stresses.
17
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Cracks
Micrography of the branch cracking parallel to the fracture. There are several secondary intergranular cracks and the cracks are filled with zinc. The zinc appears dark because of the Nital etch, and the steel close to the cracking is not fully revealed because of the protection by the zinc.
41
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Nital Etched Micrography by OMDf - Cracks
As polished micrography of the longitudinal section of the stud at the cracking transverse to the axis. It looks like inclusions/possible banding regions are contributing for the cracking.
35
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Cracks
Micrographic aspect of opened cracks, filled with oxides.
63
VIEW
ML00071 / Jan.2019
Reheating Cracking of a CrMo Vessel Weld
M - CrMo SteelP - In Field WeldAp - EnergyCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Cracks
Through wall cracking in the longitudinal seam weld of the fitting. Several cracks, longitudinal to the weld, were created by the connection of voids in the weld metal, associated to a strong microstructural evolution.
191
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Cracks
Cold cracking of the fillet weld adopted to attach a flat support into a vessel shell in the internal side, using an unsuitable welding procedure that created a too high hardness HAZ.
123
VIEW
ML00008 / Nov.2017
Cold Cracks in CMn Steel Pressure Vessel
M - CMn SteelP - In Field WeldAp - BoilerCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Cracks

More from these cases

ML00138 — Liquid Metal Embrittlement of a HSLA SteelM - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Micrographic detail of the intergranular cracks.
44
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Nital Etched Micrography by OMDf - Cracks
ML00136 — Hydrogen Cracks of Subsea StudsM - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
As polished micrography of the longitudinal section of the stud at the cracking transverse to the axis. It looks like inclusions/possible banding regions are contributing for the cracking.
33
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Cracks
As polished micrography of the longitudinal section of the stud at the cracking transverse to the axis. It looks like inclusions/possible banding regions are contributing for the cracking.
37
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Cracks
As polished micrography of the longitudinal section of the stud at the cracking transverse to the axis. It looks like inclusions/possible banding regions are contributing for the cracking and there are regions propagating witha ductile mechanism (a network of cracks in the left side of the figure).
34
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Cracks
Micrographic detail of the bottom of the thread fillet, presenting secondary cracks of intergranular morphology.
35
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Cracks
Micrography of the bottom of the thread fillet, presenting secondary cracks of intergranular morphology, propagating transverse to the stud axis, but presenting longitudinal openings in inclusions.
28
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Cracks
ML00071 — Reheating Cracking of a CrMo Vessel WeldM - CrMo SteelP - In Field WeldAp - EnergyCd - Welding Defect
Micrographic details of opened cracks, filled with oxides.
56
VIEW
ML00071 / Jan.2019
Reheating Cracking of a CrMo Vessel Weld
M - CrMo SteelP - In Field WeldAp - EnergyCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Cracks
Micrographic aspect of thin cracks.
59
VIEW
ML00071 / Jan.2019
Reheating Cracking of a CrMo Vessel Weld
M - CrMo SteelP - In Field WeldAp - EnergyCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Cracks
Micrographic details of thin cracks.
63
VIEW
ML00071 / Jan.2019
Reheating Cracking of a CrMo Vessel Weld
M - CrMo SteelP - In Field WeldAp - EnergyCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Cracks
ML00008 — Cold Cracks in CMn Steel Pressure VesselM - CMn SteelP - In Field WeldAp - BoilerCd - Welding Defect
Cold cracking of the fillet weld adopted to attach a flat support into a vessel shell in the internal side, using an unsuitable welding procedure that created a too high hardness HAZ. The cracks are mainly located at the fusion line.
118
VIEW
ML00008 / Nov.2017
Cold Cracks in CMn Steel Pressure Vessel
M - CMn SteelP - In Field WeldAp - BoilerCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Cracks
Cold cracking of the fillet weld adopted to attach a flat support into a vessel shell in the internal side, using an unsuitable welding procedure that created a too high hardness HAZ. Several internal cracks at the fusion line.
101
VIEW
ML00008 / Nov.2017
Cold Cracks in CMn Steel Pressure Vessel
M - CMn SteelP - In Field WeldAp - BoilerCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Cracks
Cold cracking of the fillet weld adopted to attach a flat support into a vessel shell using an unsuitable welding procedure, with a low preheating and no PWHT. Cracks propagated in the heat affected zone.
99
VIEW
ML00008 / Nov.2017
Cold Cracks in CMn Steel Pressure Vessel
M - CMn SteelP - In Field WeldAp - BoilerCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Cracks
Cold cracking of the fillet weld adopted to attach a flat support into a vessel shell using an unsuitable welding procedure, with a low preheating and no PWHT. Cracks propagated in the weld metal.
100
VIEW
ML00008 / Nov.2017
Cold Cracks in CMn Steel Pressure Vessel
M - CMn SteelP - In Field WeldAp - BoilerCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Cracks