Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Brittle Behavior Detail focus: Cracks clear all

Optical Microscope — sub-branches

As polished micrography 2Nital Etched Micrography by OM 2

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic details of cracks with brittle aspect (straight and multiple cracks).
42
VIEW
ML00161 / Mar.2020
Brittle Fracture of a High Strength Socket
M - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Cm - As polished micrographyDf - Cracks
Micrography of the branch cracking parallel to the fracture. There are several secondary intergranular cracks and the cracks are filled with zinc. The zinc appears dark because of the Nital etch, and the steel close to the cracking is not fully revealed because of the protection by the zinc.
40
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Nital Etched Micrography by OMDf - Cracks

More from these cases

ML00161 — Brittle Fracture of a High Strength SocketM - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Micrographic details of cracks with brittle aspect (straight and multiple cracks).
2
VIEW
ML00161 / Mar.2020
Brittle Fracture of a High Strength Socket
M - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Cm - As polished micrographyDf - Cracks
ML00138 — Liquid Metal Embrittlement of a HSLA SteelM - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Micrographic detail of the intergranular cracks.
44
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - Nital Etched Micrography by OMDf - Cracks