Optical Microscope

11 cases · 45 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Structure Detail focus: Sampling and Analysis clear all

Optical Microscope — sub-branches

As polished micrography 8Nital Etched Micrography by OM 37

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of a longitudinal section of the tube, in the center of the thickness. ND 3". 7.6 mm thick.
43
VIEW
ML00090 / Sep.2017
Carbon Steel Tubing for Structural Application
M - Low Carbon SteelP - TubeAp - StructureCd - Typical manufacturing
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Tempered martensitic structure of the plate base metal.
93
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Base Metal
Micrography of a section transverse to the Oxygen Plasma Cut surface, showing the zone affected by the heat generated in the cutting. The extension of the HAZ is about 0.5 mm. The cut was conducted in the 1 1/4" thickness of the plate.
359
VIEW
ML00033 / Jan.2017
Plasma Cut of 1 1/4" Steel Plate
M - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone

More from these cases

ML00010 — Cold Cracks in a Gouged Weld MetalM - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Detail of the tempered martensitic structure of the plate base metal. Hardness level of 27 HRc.
92
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Base Metal
Low magnification micrography of a transverse section of the weld at the heat affected zone region. The macrosection was hardness tested and the base metal hardness is 27HRc, the HAZ is 32HRc and the weld metal is 45HRc, revealing something wrong in the weld metal at the position close to the cracked area.
79
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Transverse Section
High temperature heat affected zone of the plate, welded in repair. The micrography was taken from a sample collected close to the cracked region, but not containing any macroscopic cracking.
76
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Detail of the high temperature heat affected zone of the plate, welded in repair.
69
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
The weld metal, hard, presented a martensitic structure, probably due to the localized increase in carbon content, from the unsuitable carbon arc gouging procedure.
63
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Weld Metal

+1 more from this case →

ML00033 — Plasma Cut of 1 1/4" Steel PlateM - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Intercritical heating at 0.5 mm from the cut surface, showing martensitic islands.
32
VIEW
ML00033 / Jan.2017
Plasma Cut of 1 1/4" Steel Plate
M - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Intercritical heating at 0.5 mm from the cut surface, showing martensitic islands.
27
VIEW
ML00033 / Jan.2017
Plasma Cut of 1 1/4" Steel Plate
M - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone
Location of the microhardness tests. The three measurements at the plate base metal showed average hardness of 204 HV 50g. The three measurements of the martensitic structure at the surface showed average 454HV 50g. The intercritical region showed average 324 HV 50g.
25
VIEW
ML00033 / Jan.2017
Plasma Cut of 1 1/4" Steel Plate
M - High Strength Low AlloyP - Rolled PlateAp - StructureCd - Cutting
Cm - Nital Etched Micrography by OMDf - Heat Affected Zone