Optical Microscope

1 case · 18 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Ship Microstructure: Duplex Ferritic Austenitic clear all

Optical Microscope — sub-branches

As polished micrography 7NaOH Electrolytic Etched Micro 11

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of a longitudinal section of the sleeve, at the external surface where there are two layers of coating. The electrolytic etch evidenced the duplex stainless steel substrate (bottom of the figure) and the weave interface of the substrate and the first thermal spray layer, about 1 mm thick, in a stainless steel. The surface layer, of tugnsten carbide, about 0.2 mm thick, is black and not clearly visible in this figure.
50
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - NaOH Electrolytic Etched MicroDf - External Surface

More from these cases

ML00147 — WC Layer Detached from a Cast Lean DuplexM - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Micrography of a longitudinal section of the sleeve close to the external surface, evidencing a tugnsten carbide thermal spray layer, thickness about 0.2 mm, at the sleeve outer diameter (OD), black due to the etch (top of the figure). This WC layer was deposited over a stainless steel layer disposed in several layers, non etched.
42
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - NaOH Electrolytic Etched MicroDf - Thermal Spray Layer
Micrographic detail of the interface between the two thermal spray layers, the first one in stainless steel (bottom of the figure) and the second one, at the surface,in tungsten carbide (top of the figure). The micrographic sample is etched and that is why the WC is dark (black) and the stainless steel is light (non etched).
41
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - NaOH Electrolytic Etched MicroDf - Thermal Spray Layer
Micrography of the longitudinal section of the sleeve, at the interface between the substrate and the first thermal spray layer. The substrate (bottom of the figure) shows a ferritic-austenitic microstructure and detrimental phases that look like sigma. The thermal spray layer (top of the figure) presents the non-etched stainless steel, disposed in layers, with oxides (gray) and voids (black). The substrate is deformed in a thin layer at the interface.
38
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - NaOH Electrolytic Etched MicroDf - Close to the External Surface
Micrographic detail of the interface between the substrate and the first thermal spray layer. The substrate (bottom of the figure) shows a ferritic-austenitic microstructure and detrimental phases that look like sigma at the delta and gamma interface. The thermal spray layer (top of the figure) presents the non-etched stainless steel, disposed in layers, with oxides (gray) and voids (black). The substrate is deformed in a thin layer at the interface.
34
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - NaOH Electrolytic Etched MicroDf - Sigma
Micrography of the longitudinal section of the cast sleeve in the middle of the thickness. The microstructure is coarse, austenitic ferritic.
34
VIEW
ML00147 / Aug.2018
WC Layer Detached from a Cast Lean Duplex
M - Lean Duplex Stainless SteelP - Centrifugal CastingAp - ShipCd - Lack of Sealing
Cm - NaOH Electrolytic Etched MicroDf - In the Center of the Thickness

+12 more from this case →