Optical Microscope

2 cases · 18 images for “stress corrosion”

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Oil and Gas clear all

Optical Microscope — sub-branches

As polished micrography 3FeCl3+HCl+H2O Etched Micro 7Nital Etched Micrography by OM 1Oxalic Acid Electrolytic Etch 7

Results

SortRelevanceNewestOldestTitle A-ZTitle Z-A
Micrography of the tranverse section of the tube, in the center of the thickness. There are small grains and large grains, characterizing a dual grain size. The large grains size is about 100 microns, more than 10 times larger than the average size of the smaller grains size.
101
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - FeCl3+HCl+H2O Etched MicroDf - Dual grain sizes
Optical micrography of a longitudinal section of the fractured bolt, at the thread. The material is austenitic, free from carbides, and the threads were almost removed by the stress corrosion cracks.
756
VIEW
ML00157 / Feb.2020
Bolts Under Chloride SCC Conditions
M - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Stress Corrosion Cracks

More from these cases

ML00165 — SCC of Aluminum Bronze Heating CoilM - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Micrographic detail of the alpha microstructure presenting dual grain sizes. Two different types of twins are presented in the structure: annealing twins and deformation twins, suggesting that the material was probably partially recristalized after cold deformation and stress relief treatment.
87
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - FeCl3+HCl+H2O Etched MicroDf - Alpha
Micrography of a transverse section of the bent tube, external surface (OD) to the top and internal surface (ID) to the bottom of the figure. At the through wall cracking position, the external surface presented a layer of intergranular corrosion.
95
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - As polished micrographyDf - Cracking
Micrographic detail of the external side of the bent tube, as polished, showing detachement of several grains due to the intergranular corrosion layer. The corroded layer is about 200 microns thick at this position.
89
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - As polished micrographyDf - Intergranular Corrosion
Micrographic detail of the external side of the tube, showing the layer of intergranular corrosion and the through ewall integranular stress corrosion cracking.
88
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - As polished micrographyDf - Through Wall Cracking
Micrography of the external side of the bent tube, showing detachement of several grains due to intergranular corrosion. The corroded layer is about 200 microns thick at this position. The differences of colours in the corroded layer suggests a dealloying effect, also known as selective leaching.
71
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - FeCl3+HCl+H2O Etched MicroDf - External Surface

+4 more from this case →

ML00157 — Bolts Under Chloride SCC ConditionsM - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Low magnification micrography, by optical microscope, of the longitudinal section of a damaged bolt, in the center of the thickness. The microstructure is austenitic, free from carbides.
100
VIEW
ML00157 / Feb.2020
Bolts Under Chloride SCC Conditions
M - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Austenite
Micrography, by optical microscope, of the longitudinal section of a damaged bolt, in the center of the thickness. The microstructure is austenitic, free from carbides, strain hardened. The hardness values of the material are from 200HV1 to 300HV1, that meets the class 2 of strenght (ASTM A193 B8M class 2).
79
VIEW
ML00157 / Feb.2020
Bolts Under Chloride SCC Conditions
M - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Cm - Nital Etched Micrography by OMDf - Strain Hardened
Detail of the strain hardened austenitic microstructure. Micrography by optical microscope, of the longitudinal section of a bolt, in the center of the thickness.
76
VIEW
ML00157 / Feb.2020
Bolts Under Chloride SCC Conditions
M - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Strain Hardened
Optical micrography of a longitudinal section of the fractured bolt, at the thread. The material is austenitic, free from carbides, and the threads were fully cracked by the stress corrosion mechanism.
58
VIEW
ML00157 / Feb.2020
Bolts Under Chloride SCC Conditions
M - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Stress Corrosion Cracks
Optical micrography of a longitudinal section of the fractured bolt, under the thread, showing stress corrosion cracks through the section.
46
VIEW
ML00157 / Feb.2020
Bolts Under Chloride SCC Conditions
M - Austenitic Stainless SteelP - BoltAp - Oil and GasCd - Stress Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Stress Corrosion Cracks

+2 more from this case →