Optical Microscope

2 cases · 24 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Oil and Gas Condition: Brittle Behavior Microstructure: Tempered Martensite clear all

Optical Microscope — sub-branches

As polished micrography 3Nital Etched Micrography by OM 21

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of a longitudinal section of the socket at the position where the fracture occurred. Uniform tempered martensitic structure. The hardness of this microstructure is 639 HV1Kg.
74
VIEW
ML00161 / Mar.2020
Brittle Fracture of a High Strength Socket
M - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Martensite
Micrography of a transverse section of the lifting part, showing interdendritic voids close to the surface at the inner diameter of the padeye. The microstructure is tempered martensite.
450
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Casting defects

More from these cases

ML00161 — Brittle Fracture of a High Strength SocketM - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Micrography of a longitudinal section presenting an uniform tempered martensitic structure.
81
VIEW
ML00161 / Mar.2020
Brittle Fracture of a High Strength Socket
M - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Martensite
Micrographic detail of the tempered martensitic structure.
80
VIEW
ML00161 / Mar.2020
Brittle Fracture of a High Strength Socket
M - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Martensite
Micrography, as polished, of the socket in a section transverse to the fracture, showing the fracture in the top and secondary brittle cracks.
45
VIEW
ML00161 / Mar.2020
Brittle Fracture of a High Strength Socket
M - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Cm - As polished micrographyDf - Secondary Cracks
Micrographic details of cracks with brittle aspect (straight and multiple cracks).
42
VIEW
ML00161 / Mar.2020
Brittle Fracture of a High Strength Socket
M - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Cm - As polished micrographyDf - Cracks
Micrography of the socket in a section transverse to the fracture, showing the fracture in the top and some secondary brittle cracks.
42
VIEW
ML00161 / Mar.2020
Brittle Fracture of a High Strength Socket
M - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Secondary Cracks

+4 more from this case →

ML00098 — Brittle Fracture of a Casting Lifting DeviceM - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Micrography of the lifting padeye showing a dendritic path of a quenched and tempered martensitic microstructure. The segregated regions (white interdendritic regions) are more clearly identified in low magnification. Voids are located in these segregated regions.
21
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Martensite
Micrography of the lifting padeye showing a quenched and tempered martensitic microstructure. Voids are located in interdendritic segregated regions.
20
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Martensite
Micrography of the lifting padeye showing a quenched and tempered martensitic microstructure. Voids are located in interdendritic segregated regions. At this magnification the segregation is not clear.
16
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Martensite
Micrography of the lifting padeye showing a quenched and tempered martensitic microstructure. The hardness level of the material is about 39 HRc.
14
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Martensite
Micrography of the secondary crack, paralel to fracture, starting from the internal diameter of the padeye. The crack propagates in an interdendritic morphology, interconnecting casting defects.
13
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Secondary Cracks

+8 more from this case →