Optical Microscope

2 cases · 9 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Mechanical Industry Microstructure: Tempered Martensite clear all

Optical Microscope — sub-branches

Micro by OM, picric acid+FeCl3+H2O etch 3Nital Etched Micrography by OM 6

Results

SortNewestOldestTitle A-ZTitle Z-A
Low magnification micrography presenting segregation bands in a martensitic structure. In the segregated regions the Nital etch effect is lower and the bands appear lighter. The black spots and lines are inclusions (some elongated) in the band.
91
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Micrography of the tool steel, in the longitudinal section of the part. The material presented a uniform structure, tempered martensite. The tempering was in low temperature since the hardness is high (58 HRc at the surface).
87
VIEW
ML00084 / Mar.2020
Walrus Tool Steel
M - High Carbon Tool SteelP - ForgingAp - Mechanical IndustryCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Uniform Structure

More from these cases

ML00182 — Brittle Fracture of a LAS Fixing RodM - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Micrography presenting segregation bands (less etched) in a tempered martensitic microstructure.
81
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Segregated Regions
Micrography presenting a tempered martensitic microstructure, with light etch in segregated bands.
74
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Tempered Martensite
Low magnification micrography, revealing (in black) the impurities in the segregated bands.
63
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Micro by OM, picric acid+FeCl3+H2O etchDf - Longitudinal Section
Micrographic detail of the segregated bands.
61
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Micro by OM, picric acid+FeCl3+H2O etchDf - Segregated Regions
Micrographic etch for revealing previous austenite grain boundaries, that shows the impurities.
54
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Micro by OM, picric acid+FeCl3+H2O etchDf - Segregated Regions

+1 more from this case →

ML00084 — Walrus Tool SteelM - High Carbon Tool SteelP - ForgingAp - Mechanical IndustryCd - Removed From Service
Micrographic detail of the tool steel, in the longitudinal section of the part. The material presented a uniform structure, tempered martensite, with small secondary carbides. The hardness in the section is 59 HRc.
73
VIEW
ML00084 / Mar.2020
Walrus Tool Steel
M - High Carbon Tool SteelP - ForgingAp - Mechanical IndustryCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Martensite