Optical Microscope

2 cases · 7 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Chemical Industry Standard: AISI Detail focus: Damage clear all

Optical Microscope — sub-branches

As polished micrography 3Oxalic Acid Electrolytic Etch 4

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the stub end longitudinal section, presenting multiple cracks, branched.
40
VIEW
ML00168 / Aug.2020
SCC of Austenitic SS Flange Stub End
M - Austenitic Stainless SteelP - Stub EndAp - Chemical IndustryCd - Stress Corrosion
Cm - As polished micrographyDf - Multiple cracks
SAMPLE 1 AT THE FRACTURE - Micrographic detail of the intergranular fracture. The austenitic grains of the material are loosing.
80
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - Oxalic Acid Electrolytic EtchDf - Intergranular Fracture

More from these cases

ML00168 — SCC of Austenitic SS Flange Stub EndM - Austenitic Stainless SteelP - Stub EndAp - Chemical IndustryCd - Stress Corrosion
Micrography of the stub end longitudinal section, showing multiple branched transgranular cracks.
25
VIEW
ML00168 / Aug.2020
SCC of Austenitic SS Flange Stub End
M - Austenitic Stainless SteelP - Stub EndAp - Chemical IndustryCd - Stress Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Transgranular Cracking
Micrography of the stub end longitudinal section, showing multiple branched transgranular cracks, typical of a Chloride Stress Corrosion Cracking mechanism.
34
VIEW
ML00168 / Aug.2020
SCC of Austenitic SS Flange Stub End
M - Austenitic Stainless SteelP - Stub EndAp - Chemical IndustryCd - Stress Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Corrosion Cracking
Micrographic details of the Chloride Stress Corrosion Cracks, transgranular and branched.
34
VIEW
ML00168 / Aug.2020
SCC of Austenitic SS Flange Stub End
M - Austenitic Stainless SteelP - Stub EndAp - Chemical IndustryCd - Stress Corrosion
Cm - Oxalic Acid Electrolytic EtchDf - Corrosion Cracking
ML00160 — High Temperature Degradation of 310SSM - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
SAMPLE 1, AT THE FRACTURE - Micrography, as polished, of the oxides at the fracture (zero thickness). In this region the oxide layer penetrated through thickness, intergranular, and fractured the material.
63
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - As polished micrographyDf - Intergranular Fracture
SAMPLE 1, AT THE FRACTURE - Micrographic detail, as polished, of the oxides that are penetrating in the austenitic grain boundaries. The oxidation created intergranular cracks in regions close to the edge of the rectangular tube, that are more susceptible to suffer cyclic thermal stresses, since the furnace is weekly turned off, during two days.
55
VIEW
ML00160 / Apr.2020
High Temperature Degradation of 310SS
M - Austenitic Stainless SteelP - Rectangular TubeAp - Chemical IndustryCd - Scaling
Cm - As polished micrographyDf - Intergranular Cracking