3 cases · 4 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Corrosion Fatigue clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Metallographic aspect of a longitudinal section of the clamp, at the surface (left side of the image) showing a region where there are corrosion pits in the carbon steel clamp, due to the lack of protection by the coating, and the propagation of small transgranular cracks from to the surface.
30
VIEW
ML00171 / Feb.2021
Corrosion Fatigue of U Bolt Pipe Clamp
M - Low Carbon SteelP - BoltAp - ShipCd - Corrosion Fatigue
Cm - Micrography by OMDf - Crack
Micrography of the pin in a longitudinal section, transverse to the fracture surface, at the ductile final fracture, presenting microvoids connecting with plastic deformation of the structure.
50
VIEW
ML00085 / Nov.2017
Corrosion Fatigue of a Martensitic SS Pin
M - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Micrography by OMDf - Fracture
The micrography in the as polished condition of the longitudinal section of the pipe close to the washout, shows that at the tool mark tip (notch from the external surface) a fatigue crack already started from a corroded region (pitting).
187
VIEW
ML00068 / Sep.2020
Corrosion Fatigue of a 5" Drill Pipe
M - Low Alloy Medium Carbon QTP - Seamless PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Micrography by OMDf - Pitting

More from these cases

ML00068 — Corrosion Fatigue of a 5" Drill PipeM - Low Alloy Medium Carbon QTP - Seamless PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Micrographic detail, in the as polished condition, of the corrosion fatigue crack.
89
VIEW
ML00068 / Sep.2020
Corrosion Fatigue of a 5" Drill Pipe
M - Low Alloy Medium Carbon QTP - Seamless PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Micrography by OMDf - Fatigue Crack