Kalling Etched Micrography by OM

3 cases · 20 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: S42000 clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Low magnification micrography of the nut in the longitudinal section, presenting the machined internal thread and a banded microstructure.
55
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Banded Structure
Micrography of a transverse section of the ring presenting a uniform tempered martensite structure.
43
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - Kalling Etched Micrography by OMDf - Martensite
Micrographic aspect of the corrosion damage in a section transverse to the pitting.
167
VIEW
ML00054 / Dec.2018
Cutlery Corrosion
M - Martensitic Stainless SteelP - Foodstuff ArticleAp - KitchenCd - Pitting Corrosion
Cm - Kalling Etched Micrography by OMDf - Pitting

More from these cases

ML00148 — Brittle Fracture of a 420 SS Barrel NutM - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Microstructural aspect of a longitudinal section of the nut, in the middle of the thickness. Martensitic structure, banded.
46
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Banded Structure
Microstructural detail of the banded structure. The rough aspect of the band is created by the carbides (better seen in the higher magnification image) in the segregation band.
38
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Banded Structure
Micrographic detail of the nut longitudinal section presenting the large carbides (white islands) in the segregation band, and small precipitates all through the martensite matrix, indicating that this high carbon steel was tempered in a high temperature. The 36HRc hardness also confirms this high tempering temperature.
39
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Martensite
Vickers microhardness identations using 100 grams. In a position out of the band (top line). Values from left to right, 380HV; 390HV and 394HV. In a position inside the band (bottom line). Values from left to right, 433HV, 483HV and 473 HV.
33
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Banded Structure
Low magnification micrography of the nut in the longitudinal section, presenting the machined internal thread and a banded microstructure. It is possible to see that the contact pressure in the thread caused a surface plastically deformation.
23
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Banded Structure

+6 more from this case →

ML00124 — MIC of a Martensitic Valve RingM - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Micrography of a transverse section of the ring at the cracking position. The cracks are intergranular and opened at the position close to the surface.
27
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - Kalling Etched Micrography by OMDf - Martensite
Micrography of a transverse section of the ring at the cracking position. The cracks are intergranular and opened at the position close to the surface. it is possible to identify dissolution of the structure adjacent to the grain boundaries,
25
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - Kalling Etched Micrography by OMDf - Crack
Micrographic detail of a transverse section of the ring at the cracking position. The cracks are intergranular and opened at the position close to the surface. it is possible to identify dissolution of the structure adjacent to the grain boundaries,
24
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - Kalling Etched Micrography by OMDf - Intergranular Cracking
Micrograph showing a fine acicular martensitic matrix with a branching crack network, more extensive near the right edge.
25
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - Kalling Etched Micrography by OMDf - Crack
Micrography of a transverse section of the ring, in the center, where the cracking was closed. The cracks are intergranular and not opened to the surface.
29
VIEW
ML00124 / Feb.2018
MIC of a Martensitic Valve Ring
M - Martensitic Stainless SteelP - ForgingAp - EnergyCd - Brittle Behavior
Cm - Kalling Etched Micrography by OMDf - Crack

+1 more from this case →