Kalling Etched Micrography by OM

1 case · 5 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Fastener Standard: S17400 clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic aspect of the aged martensite structure of the 17-4 PH bolt, about 37 HRc.
93
VIEW
ML00074 / Jun.2018
Hydrogen Cracking of a 17-4 PH Subsea Bolt
M - Precipitation Hardened Stainless SteelP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Martensite

More from these cases

ML00074 — Hydrogen Cracking of a 17-4 PH Subsea BoltM - Precipitation Hardened Stainless SteelP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Micrographic detail of the aged martensite structure of the 17-4 PH bolt, about 37 HRc.
72
VIEW
ML00074 / Jun.2018
Hydrogen Cracking of a 17-4 PH Subsea Bolt
M - Precipitation Hardened Stainless SteelP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Martensite
Micrography of the longitudinal section of the bolt, at the bottom of the thread fillet, showing that the fracture is intergranular in this position.
71
VIEW
ML00074 / Jun.2018
Hydrogen Cracking of a 17-4 PH Subsea Bolt
M - Precipitation Hardened Stainless SteelP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Longitudinal Section
Micrographic detail of intergranular cracks close to the fracture of the bolt, near the bolt surface where the macroscopi aspect was brittle.
82
VIEW
ML00074 / Jun.2018
Hydrogen Cracking of a 17-4 PH Subsea Bolt
M - Precipitation Hardened Stainless SteelP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Intergranular Cracking
Micrographic detail of the longitudinal cracks in the middle of the bolt, that generaate the secondary cracks that appear at the fracture surface.
79
VIEW
ML00074 / Jun.2018
Hydrogen Cracking of a 17-4 PH Subsea Bolt
M - Precipitation Hardened Stainless SteelP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Intergranular Cracking