Kalling Etched Micrography by OM

3 cases · 7 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Detail focus: Transverse Section clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
The transverse section of the spring wire shows a strain hardened martensitic structure, aged to high strength (602 HV 0.3kg).
48
VIEW
ML00076 / Jun.2017
Hydrogen Cracking of a 17-7 PH Subsea Spring
M - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Transverse Section
13Cr SS in the transverse section, at the collapsed region, showing a non uniform structure that evidences an usuitable heat treatment during fabrication, and explains the material low strenght.
29
VIEW
ML00039 / Apr.2017
Collapse in Tubular 13Cr
M - Martensitic Stainless SteelP - Seamless PipeAp - Oil and GasCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Transverse Section
Equiaxial grains of a ferritic structure, in a transverse section of the tube.
40
VIEW
ML00026 / Feb.2017
Autogenous Seam Welded Tube in Ferritic SS
M - Ferritic Stainless SteelP - Fabrication WeldAp - AutomotiveCd - Typical manufacturing
Cm - Kalling Etched Micrography by OMDf - Transverse Section

More from these cases

ML00076 — Hydrogen Cracking of a 17-7 PH Subsea SpringM - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Micrographic detail of the strain hardened aged martensitic structure.
48
VIEW
ML00076 / Jun.2017
Hydrogen Cracking of a 17-7 PH Subsea Spring
M - Precipitation Hardened Stainless SteelP - WireAp - SubseaCd - Hydrogen Embrittlement
Cm - Kalling Etched Micrography by OMDf - Transverse Section
ML00039 — Collapse in Tubular 13CrM - Martensitic Stainless SteelP - Seamless PipeAp - Oil and GasCd - Heat Treatment Defect
13Cr SS transverse section micrography, at the collapsed region, showing a ferritic matrix structure (overtempered) with the previous austenite grain boundaries decorated by phases (carbides and probably martensite islands), indicating that the material was exposed to a high tempering temperature that created a partial austenitizing condition. It explains the material low toughness and lower strenght (than required).
29
VIEW
ML00039 / Apr.2017
Collapse in Tubular 13Cr
M - Martensitic Stainless SteelP - Seamless PipeAp - Oil and GasCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Transverse Section
The micrography of the 13Cr SS in the transverse section, far from the collapsed region, shows a uniform tempered martensitic structure.
27
VIEW
ML00039 / Apr.2017
Collapse in Tubular 13Cr
M - Martensitic Stainless SteelP - Seamless PipeAp - Oil and GasCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Transverse Section
The micrography of the 13Cr SS in the transverse section, far from the collapsed region, shows a uniform tempered martensitic structure.
26
VIEW
ML00039 / Apr.2017
Collapse in Tubular 13Cr
M - Martensitic Stainless SteelP - Seamless PipeAp - Oil and GasCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Transverse Section