FeCl3+HCl+H2O Etched Micro

6 cases · 17 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Detail focus: Microstructure clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic detail of the granular copper structure, a little far from the overheated region.
102
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - FeCl3+HCl+H2O Etched MicroDf - Granular structure
Low magnification micrography of a transverse section of the ring showing a dendritic structure.
64
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Dendritic
Micrography of the tranverse section of the tube, in the center of the thickness. There are small grains and large grains, characterizing a dual grain size. The large grains size is about 100 microns, more than 10 times larger than the average size of the smaller grains size.
101
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - FeCl3+HCl+H2O Etched MicroDf - Dual grain sizes
dddd
4
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - FeCl3+HCl+H2O Etched MicroDf - Bainite
The material structure is monophasic.
110
VIEW
ML00043 / Apr.2017
CuNi Condenser Tube
M - CupronickelP - Seamless tubeAp - Heat ExchangerCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Single phase
The micrography of the pin far from the fracture surface shows a biphasic brass, and Pb inclusions that are intentional to give a free machining condition for the alloy.
76
VIEW
ML00007 / Dec.2020
Free Machining Brass in Shear Pin
M - BrassP - Machined PartAp - LiftingCd - Shear
Cm - FeCl3+HCl+H2O Etched MicroDf - Two phases

More from these cases

ML00180 — Local Melting of Copper Cooling TubesM - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Micrographic detail of the granular copper structure, out of the damaged area. The dark particles are non metallic (oxides).
93
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - FeCl3+HCl+H2O Etched MicroDf - Granular structure
Micrographic aspect of the tube wall under the localized thinning, in a transverse section, showing a coarse structure due to high temperature grain growth.
38
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - FeCl3+HCl+H2O Etched MicroDf - Overheating
Micrographic detail of the high temperature grain growth in the tube microstructure.
31
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - FeCl3+HCl+H2O Etched MicroDf - Coarse Structure
Micrographic detail of the high temperature grain growth in the tube microstructure.
35
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - FeCl3+HCl+H2O Etched MicroDf - Coarse Structure
Local Melting of Copper Cooling Tubes
4
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - FeCl3+HCl+H2O Etched MicroDf - Overheating
ML00166 — Tin Bronze Wear Ring of Seawater PumpM - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Micrography of a transverse section of the ring showing a cored alpha structure with segregation at interdendritic regions. This structure is in a region close to the ring surface.
52
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Dendritic
Micrography of a transverse section of the ring showing a cored alpha structure with strong segregation at interdendritic regions, and regions of a white structure at grain boundaries. This structure is in a region close to the center of the ring.
51
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Dendritic
Micrographic detail of the cored alpha structure with light segregation at intergranular regions (light layer at grain boundaries), and a white euctetoid structure (alpha and delta) at interdendritic space. This structure is in a region close to the ring surface, where the solidification was quicker.
49
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Grain boundary intermetallics
Micrographic detail of the cored alpha structure with strong segregation at intergranular regions (dark layer at grain boundaries), and a white euctetoid structure (alpha and delta) at interdendritic space. This structure is in a region close to the center of the ring, where the solidification was slower.
47
VIEW
ML00166 / Jul.2020
Tin Bronze Wear Ring of Seawater Pump
M - Tin BronzeP - Wear RingAp - ShipCd - Removed From Service
Cm - FeCl3+HCl+H2O Etched MicroDf - Grain boundary intermetallics
ML00165 — SCC of Aluminum Bronze Heating CoilM - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Micrographic detail of the alpha microstructure presenting dual grain sizes. Two different types of twins are presented in the structure: annealing twins and deformation twins, suggesting that the material was probably partially recristalized after cold deformation and stress relief treatment.
87
VIEW
ML00165 / Jul.2020
SCC of Aluminum Bronze Heating Coil
M - Aluminum BronzeP - Seamless tubeAp - Oil and GasCd - Stress Corrosion
Cm - FeCl3+HCl+H2O Etched MicroDf - Alpha
ML00155 — Failure of a Prestressed Concrete Steel StrandM - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
teste
3
VIEW
ML00155 / Jan.2020
Failure of a Prestressed Concrete Steel Strand
M - High Carbon SteelP - Wire RopeAp - StructureCd - Corrosion Fatigue
Cm - FeCl3+HCl+H2O Etched MicroDf - Bainitic HAZ