As polished micrography

5 cases · 9 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Detail focus: Cracks clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic aspect, as polished, of a transverse section of the tube (bottom side of the image, orange), at the interface between the tube and the melted steel over the external diameter (top side of the image, grey). In the copper tube there are several microcracks and regions of incipient melting (voids).
41
VIEW
ML00180 / Mar.2022
Local Melting of Copper Cooling Tubes
M - Pure CopperP - Cooling TubeAp - SiderurgyCd - Overheating
Cm - As polished micrographyDf - Cracks
Micrographic details of cracks with brittle aspect (straight and multiple cracks).
42
VIEW
ML00161 / Mar.2020
Brittle Fracture of a High Strength Socket
M - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Cm - As polished micrographyDf - Cracks
As polished micrography of the longitudinal section of the stud at the cracking transverse to the axis. It looks like inclusions/possible banding regions are contributing for the cracking.
35
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Cracks
Micrography of the longitudinal section of the stud showing internal cracks, secondary (not the cracks that opened the fracture). It is evident that the cracking from the thread fillet, of a ductile aspect, presented a different aspect than the internal cracks, of a brittle aspect.
31
VIEW
ML00127 / May.2018
Hydrogen Cracks of Cadmium Plated Studs
M - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Cracks
Micrographic detail of the dezincification effect, where the beta phase is preferentially corroded, leaving a cooper rich phase (red) that is porous and easily cracks.
130
VIEW
ML00125 / Mar.2018
Dezincification of a Cooler Tubesheet
M - BrassP - PlateAp - ShipCd - Preferential Dissolution
Cm - As polished micrographyDf - Cracks

More from these cases

ML00161 — Brittle Fracture of a High Strength SocketM - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Micrographic details of cracks with brittle aspect (straight and multiple cracks).
2
VIEW
ML00161 / Mar.2020
Brittle Fracture of a High Strength Socket
M - Medium Carbon Tool SteelP - ToolAp - Oil and GasCd - Brittle Fracture
Cm - As polished micrographyDf - Cracks
ML00136 — Hydrogen Cracks of Subsea StudsM - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
As polished micrography of the longitudinal section of the stud at the cracking transverse to the axis. It looks like inclusions/possible banding regions are contributing for the cracking.
33
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Cracks
As polished micrography of the longitudinal section of the stud at the cracking transverse to the axis. It looks like inclusions/possible banding regions are contributing for the cracking.
37
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Cracks
As polished micrography of the longitudinal section of the stud at the cracking transverse to the axis. It looks like inclusions/possible banding regions are contributing for the cracking and there are regions propagating witha ductile mechanism (a network of cracks in the left side of the figure).
34
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - As polished micrographyDf - Cracks