Naked Eye or Stereoscope

2 cases · 5 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Graphite in flakes clear all

Naked Eye or Stereoscope — sub-branches

Fracture Surface Aspect 3NItal Etched Macro 2

Results

SortNewestOldestTitle A-ZTitle Z-A
Fractured position of the casting cylinder of 10.5 mm thickness (minimum measured thickness) showing a brittle behavior (lack of plastic deformation), typical of overloading a material with 1% ductility (measured in the tensile test). This is the view of the internal surface of the cylinder, presenting regions of localized thinning in this surface that was in contact with (treated) cooling water. The external side of the cylinder was painted.
918
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Fracture Surface AspectDf - General View
The macrography of a longitudinal section of the camshaft (tubular) in a position where there are two chilled lobes, presenting a strong microstructural change through thickness, from the hard chilled surface (500HV10) to the soft region in the middle of the thickness (187HV10).
96
VIEW
ML00060 / Apr.2017
Brittle Fracture of a Chilled Cast Iron Camshaft
M - Chilled Cast IronP - ShaftAp - AutomotiveCd - Brittle Fracture
Cm - NItal Etched MacroDf - Longitudinal Section

More from these cases

ML00141 — Brittle Fracture of a Corroded Gray Cast IronM - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Fracture aspect of the casting cylinder at the 10.5 mm thickness, showing a brittle behavior (lack of plastic deformation). The internal side of the cylinder is to the top of the figure, and the painted surface is to the bottom of the figure.
129
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Fracture Surface AspectDf - Brittle Fracture
Detailed aspect of the cylinder fracture, the internal surface to the top of the figure and the painted external surface to the bottom of the figure.
103
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - Fracture Surface AspectDf - Brittle Fracture
Macrographic aspect of a section of the cast cylinder, transverse to the fracture (top). The internal diameter of the cylinder (exposed to treated water) is to the left side and the external diameter of the cylinder (painted) is to the right side.
96
VIEW
ML00141 / Jul.2018
Brittle Fracture of a Corroded Gray Cast Iron
M - Gray Cast ironP - CastingAp - EngineCd - Brittle Fracture
Cm - NItal Etched MacroDf - Brittle Fracture