NItal Etched Macro

3 cases · 7 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Mechanical Industry clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Macrography of a section transverse to the fracture, at the surface of the casting. It is possible to see the large thickness of the galvanized layer at the surface (left side of the figure). There is a white layer over the fracture surface (top of the figure) and branch cracks starting from the surface, parallel to the fracture (in the bottom left side of the figure).
68
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - NItal Etched MacroDf - Secondary Cracks
Macrography of a circumferential section of the roller bearing, showing two different structures: one, white and hard (64 HRc), close to the external surface; and the other, dark and soft (21 HRc), close to the internal surface. The hardness in the thickness, close to the interface, is about 50 HRc.
122
VIEW
ML00131 / Apr.2018
Brittle Failure of a Soft Roller Bearing
M - Wear Resistant SteelP - Roller BearingAp - Mechanical IndustryCd - Heat Treatment Defect
Cm - NItal Etched MacroDf - Duplex structure
The macrography of the transverse tooth section of the SPUR GEAR shows that the surface is not hardened by any process or treatment.
105
VIEW
ML00027 / Apr.2017
Adhesive Wear of Spur Gear Rack
M - Medium Carbon SteelP - Spur GearAp - Mechanical IndustryCd - Adhesive Wear
Cm - NItal Etched MacroDf - Non Hardened Surface

More from these cases

ML00138 — Liquid Metal Embrittlement of a HSLA SteelM - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Macrographic detail of the branch cracks starting from the surface, parallel to the fracture.
64
VIEW
ML00138 / Jun.2018
Liquid Metal Embrittlement of a HSLA Steel
M - High Strength Low AlloyP - Coated ProductAp - Mechanical IndustryCd - Liquid Metal Embrittlement
Cm - NItal Etched MacroDf - Secondary Cracks
ML00027 — Adhesive Wear of Spur Gear RackM - Medium Carbon SteelP - Spur GearAp - Mechanical IndustryCd - Adhesive Wear
A detail of the macrography, by stereoscope, of the SPUR RACK shows strong plastic deformation at the contact surface.
88
VIEW
ML00027 / Apr.2017
Adhesive Wear of Spur Gear Rack
M - Medium Carbon SteelP - Spur GearAp - Mechanical IndustryCd - Adhesive Wear
Cm - NItal Etched MacroDf - Plastic Deformation
The macrography of the transverse tooth section of the SPUR GEAR shows that the surface is not hardened by any process or treatment.
43
VIEW
ML00027 / Apr.2017
Adhesive Wear of Spur Gear Rack
M - Medium Carbon SteelP - Spur GearAp - Mechanical IndustryCd - Adhesive Wear
Cm - NItal Etched MacroDf - Non Hardened Surface
A detail of the macrography, by stereoscope, of the SPUR GEAR shows strong plastic deformation at the contact surface.
37
VIEW
ML00027 / Apr.2017
Adhesive Wear of Spur Gear Rack
M - Medium Carbon SteelP - Spur GearAp - Mechanical IndustryCd - Adhesive Wear
Cm - NItal Etched MacroDf - Plastic Deformation