Micrography by OM

5 cases · 9 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Pipe clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the pipe in a longitudinal section, close to the external surface, showing a pit (adjacent to the through wall cracking). The corrosion spt is not associated to any microstructural feature.
61
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Micrography by OMDf - Pitting
The micrography in the as polished condition of the longitudinal section of the pipe close to the washout, shows that at the tool mark tip (notch from the external surface) a fatigue crack already started from a corroded region (pitting).
187
VIEW
ML00068 / Sep.2020
Corrosion Fatigue of a 5" Drill Pipe
M - Low Alloy Medium Carbon QTP - Seamless PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Micrography by OMDf - Pitting
The micrography in the as polished condition of the NEW TUBE shows that there are no casting defects close to the external surface.
49
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Micrography by OMDf - Close to the External Surface
Detail, as polished, of brittle cracks in the weld metal, from the internal side of the pipe.
67
VIEW
ML00005 / Apr.2017
Environmental Hydrogen Damage in Ti Pipe
M - Unalloyed TitaniumP - Longitudinal Seam Welded PipeAp - PipingCd - Hydride Formation
Cm - Micrography by OMDf - Brittle Cracks
Micrography of a transverse section of the pipe, presenting the pitting corrosion. As polished.
310
VIEW
ML00014 / Apr.2017
Pitting Corrosion in 316SS Pipe
M - Austenitic Stainless SteelP - Seamless PipeAp - FPSOCd - Pitting Corrosion
Cm - Micrography by OMDf - Pitting

More from these cases

ML00068 — Corrosion Fatigue of a 5" Drill PipeM - Low Alloy Medium Carbon QTP - Seamless PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Micrographic detail, in the as polished condition, of the corrosion fatigue crack.
89
VIEW
ML00068 / Sep.2020
Corrosion Fatigue of a 5" Drill Pipe
M - Low Alloy Medium Carbon QTP - Seamless PipeAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Micrography by OMDf - Fatigue Crack
ML00038 — Cast SS Tube for High Temperature ServiceM - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
The micrography in the as polished condition of the NEW TUBE shows that there are no casting defects in the center of the thickness.
47
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Micrography by OMDf - Transverse Section
Micrography, in the as polished condition, of the TUBE REMOVED FROM SERVICE, centrifugally cast, in the transverse section, presenting external surface oxides and voids.
35
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Micrography by OMDf - Voids
The micrography in the as polished condition of the TUBE REMOVED FROM SERVICE shows that after one year operating in high temperature the material opens voids in the center of the thickness. Even the secondary carbide is coalesced.
36
VIEW
ML00038 / Apr.2017
Cast SS Tube for High Temperature Service
M - Heat Resistant SteelP - Centrifugally Cast PipeAp - SiderurgyCd - Creep
Cm - Micrography by OMDf - Transverse Section