Micrography by OM using A262 Method A

3 cases · 20 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Welded Joint Standard: ASTM clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Through wall cracking in the longitudinal seam weld of the fitting. Several cracks, longitudinal to the weld, were created by the connection of voids in the weld metal, associated to a strong microstructural evolution.
191
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Cracks
Micrography of a longitudinal section of the pipe showing the stainless steel pipe , external.
100
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Micrography by OM using A262 Method ADf - Austenite
Micrographic detail of the fatigue cracking at the margin of the flange to shell fillet weld.
485
VIEW
ML00050 / Nov.2017
Fatigue Failure of a 316SS Pressure Stabilizer
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
Cm - Micrography by OM using A262 Method ADf - Fatigue Crack

More from these cases

ML00061 — Creep in a Seam Weld of a 304H SS FittingM - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Micrography of a longitudinal section of the fitting, at the base metal, presenting an austenitic structure with intergranular and transgranular precipitation as a result of microstructural evolution.
44
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Base Metal
Micrographic detail of the fitting base metal, presenting an austenitic structure with intergranular and transgranular precipitation as a result of microstructural evolution.
40
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Base Metal
Micrography of a transverse section of the seam weld, close to the internal surface, presenting several cracks perpendicular to the thickness.
37
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Close to the Internal Surface
Micrographic detail of the seam weld close to the internal surface, presenting the needles that are the result of microsctructural evolution and cracks filled with oxides.
36
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - Close to the Internal Surface
Micrography of a transverse section of the seam weld, in the middle of the thickness, presenting several parallel cracks.
27
VIEW
ML00061 / Apr.2017
Creep in a Seam Weld of a 304H SS Fitting
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Creep
Cm - Micrography by OM using A262 Method ADf - In the Center of the Thickness

+7 more from this case →

ML00056 — Seamless Tube Externally Cladded with SSM - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Micrography of the interface between the carbon steel that is strongly etched by the electrolytic oxalic acid (in the left side of the figure) and the stainless steel, in the longitudinal section of the pipe. There is a strain hardened layer very close to the interface, at the stainless steel side.
79
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Micrography by OM using A262 Method ADf - Longitudinal Section
Micrographic detail of the interface showing the strain hardened layer at the stainless steel side (in the right of the figure), revealed using the Electrolytic etch.
76
VIEW
ML00056 / May.2018
Seamless Tube Externally Cladded with SS
M - Carbon Steel / Stainless SteelP - CladdingAp - Pulp and PaperCd - Removed From Service
Cm - Micrography by OM using A262 Method ADf - Clad Interface
ML00050 — Fatigue Failure of a 316SS Pressure StabilizerM - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
The shell plate micrography showed an austenitic structure.
101
VIEW
ML00050 / Nov.2017
Fatigue Failure of a 316SS Pressure Stabilizer
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
Cm - Micrography by OM using A262 Method ADf - Austenite
The micrography of the welded joint between the flange and the shell, in a region that was through wall cracked, the fracture propagating in the shell plate base metal.
74
VIEW
ML00050 / Nov.2017
Fatigue Failure of a 316SS Pressure Stabilizer
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
Cm - Micrography by OM using A262 Method ADf - Welded Joint
The micrography of the welded joint between the flange and the shell, in a region that was not yet macroscopically cracked, presented a fatigue crack from the margin of the fillet weld.
72
VIEW
ML00050 / Nov.2017
Fatigue Failure of a 316SS Pressure Stabilizer
M - Austenitic Stainless SteelP - Fabrication WeldAp - Chemical IndustryCd - Mechanical Fatigue
Cm - Micrography by OM using A262 Method ADf - Welded Joint