Fractography by SEM

2 cases · 5 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Subsea Standard: ALLOY clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
The through wall cracking was opened by citting the two sides and the aspect was characterized by SEM. Although there was a film at the fracture surface, probably because the fitting was removed from service some time after it was leaking, the fracture micromechanism is by quasecleavage, typical of a stress corrosion cracking.
56
VIEW
ML00094 / Sep.2017
MIC of a Subsea Hydraulic Line
M - Super Duplex Stainless SteelP - Fabrication WeldAp - SubseaCd - Brittle Behavior
Cm - Fractography by SEMDf - Transgranular Fracture
Transgranular brittle aspect of the stud fracture surface. Evidences of hydrogen embrittlement.
965
VIEW
ML00075 / Jun.2018
Hydrogen Cracking of IN 718 Subsea Fasteners
M - NiCrFe AlloyP - StudAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Secondary Cracks

More from these cases

ML00075 — Hydrogen Cracking of IN 718 Subsea FastenersM - NiCrFe AlloyP - StudAp - SubseaCd - Hydrogen Embrittlement
The secondary cracks are easily observed in the fracture surface, longitudinal to the axis of the stud.
26
VIEW
ML00075 / Jun.2018
Hydrogen Cracking of IN 718 Subsea Fasteners
M - NiCrFe AlloyP - StudAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture
The fracture of the stud presented both intergranular and transgranular aspects.
26
VIEW
ML00075 / Jun.2018
Hydrogen Cracking of IN 718 Subsea Fasteners
M - NiCrFe AlloyP - StudAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Brittle Fracture
The fracture of the stud presented transgranular aspects and secondary cracks that appear to be related to small broken particles.
32
VIEW
ML00075 / Jun.2018
Hydrogen Cracking of IN 718 Subsea Fasteners
M - NiCrFe AlloyP - StudAp - SubseaCd - Hydrogen Embrittlement
Cm - Fractography by SEMDf - Secondary Cracks