Aspect Before Analysis

3 cases · 7 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: G41400 clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
The shaft was removed from service without a failure. It was 4' long and the diameters varied from 2 1/2" to 4 1/2". It was analyzed to be specified for purchasing a new one but properties evidenced bad ductility and brittle behavior even at ambient temperature, associated to a microestruture "as hot rolled".
1238
VIEW
ML00152 / Dec.2018
Low Alloy Steel Pump Shaft
M - High Strength Low AlloyP - ShaftAp - Oil and GasCd - Removed From Service
Cm - Aspect Before AnalysisDf - General View
Aspect of the broken stud that was fastening a flanged line in a subsea body (tapped hole) using a nut. The fracture, transverse to the stud axis, occurred exactly at the body to flange interface. Adjacent to the fracture, all thread fillets (positioned inside the flange hole) presented cracks at the bottom of the thread. The stud was operating during seven years and was not corroded, indicating it was protected by the anodes. There are also deposits in the fillets suggesting the cathodic protection was effective even inside the flange hole.
799
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View
Allen stud, 1/2" nominal diameter, cadmium plated and chromate treated, cracked during assembling external parts in a gate valve.
63
VIEW
ML00127 / May.2018
Hydrogen Cracks of Cadmium Plated Studs
M - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View

More from these cases

ML00136 — Hydrogen Cracks of Subsea StudsM - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Macroscopic view of the fracture surface showing that there is a flat appearance of the fracture close to the bottom of the thread (upper side of the figure) and a flat, but rough appearance in the center of the stud. No evidences of corrosion in the thread fillets indicating that the stud was protected.
59
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - Brittle Fracture
Macroscopic detail of the stud, adjacent to the fracture, showing that there are several secondary cracks at the bottom of the thread fillets, without any deformation evidence. This reveals a brittle material behavior, although the hardness measured at the stud end revealed 33HRc, as should be expected by the material specification.
59
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - Secondary Cracks
ML00127 — Hydrogen Cracks of Cadmium Plated StudsM - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Allen stud, 1/2" nominal diameter, cadmium plated and chromate treated, cracked during assembling external parts in a gate valve.
40
VIEW
ML00127 / May.2018
Hydrogen Cracks of Cadmium Plated Studs
M - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - Fracture
Allen stud, cadmium plated and chromate treated. The fracture appearance is brittle.
38
VIEW
ML00127 / May.2018
Hydrogen Cracks of Cadmium Plated Studs
M - Low Alloy Medium Carbon QTP - Allen StudAp - Oil and GasCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - Fracture