Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: class 12.9 clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of the broken bolt, 5/8" Allen, socket head cap screw, originally 1 3/4" long, broken in subsea service under cathodic protection. The bolt presents a zinc coating.
116
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View
Aspect of the fastener fracture, flat, at a thread fillet.
69
VIEW
ML00073 / Jun.2018
Hydrogen Cracking of a LAS Subsea Fastener
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View

More from these cases

ML00126 — Hydrogen Fracture of Subsea Allen BoltsM - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Aspect of the fracture of a small Allen bolt, nominal diameter 5/8" 1 3/4" long, class 12.9, that was operating in subsea environment during 5 years. The fracture is rusted but the thread still presents the zinc coating.
81
VIEW
ML00126 / Mar.2018
Hydrogen Fracture of Subsea Allen Bolts
M - Low Alloy Medium Carbon QTP - Coated ProductAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View
ML00073 — Hydrogen Cracking of a LAS Subsea FastenerM - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
One side of the broken socket head screw, presenting secondary cracks in thread fillets adjacent to the position where the nut was tightened.
64
VIEW
ML00073 / Jun.2018
Hydrogen Cracking of a LAS Subsea Fastener
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View