Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Raw Material Microstructure: Carburized Layer clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of the superheater ND 1" tube that was in operation for about 35,000 hours and presented a thick deposit at the external surface.
211
VIEW
ML00107 / Dec.2017
Carburized 9Cr1MoV Superheater Tube
M - Heat Resistant SteelP - Seamless tubeAp - BoilerCd - Carburization
Cm - Aspect Before AnalysisDf - General View
Aspect of three pins that were operating in a hydraulic system. Adjacent to the fracture of the broken pin (the one that is in the right side of the figure) it is possible to see multiple surface craks and detachment of the surface chromium layer.
88
VIEW
ML00081 / Aug.2017
Hydrogen Cracking of a Chromium Plated Carburized Pin
M - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View

More from these cases

ML00081 — Hydrogen Cracking of a Chromium Plated Carburized PinM - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
The aspect of the pin fracture surface shows that a fatigue crack propagated from the pin surface at the edge of a lubrication hole in the chromium plated pin.
83
VIEW
ML00081 / Aug.2017
Hydrogen Cracking of a Chromium Plated Carburized Pin
M - Low Alloy for Thermochemical TreatmentP - Chromium PlatedAp - AutomotiveCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - Fatigue Fracture