Aspect Before Analysis

3 cases · 6 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Dendritic Detail focus: Damage clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of a crevice corrosion of the flange, under the bolt head, showing evidences that the cathodic protection system was not connected to the stainless steel instrument.
1434
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Aspect Before AnalysisDf - Localized Corrosion
Aspect of the fracture surface, showing a brittle morphology. Flat fracture with chevron marks from regions close to the internal diameter of the padeye, where there are secondary cracks.
22
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Fracture
Region of the leakage close to the welded joint between the pipe and the 90° elbow, in the 1 1/2" nominal diameter piping, SCH 40 (3.7 mm thick). See the schematic drawing in the next figure
966
VIEW
ML00065 / May.2017
Erosion Corrosion of Monel Piping
M - NiCu AlloyP - Seamless PipeAp - Chemical IndustryCd - Erosion Corrosion
Cm - Aspect Before AnalysisDf - Leakage

More from these cases

ML00122 — Crevice Corrosion in a Subsea SystemM - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Detail of the electronic device after removing the external case. It is corroded because seawater entered in the equipment that was pressurized from the external sea environment.
228
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Aspect Before AnalysisDf - Corrosion
The case where the electronic device was installed suffered a localized corrosion that allowed the seawater to wet the internal side, destroying it. The position where the leakage occurred originally presented a hole that was sealed with a plug and the corrosion occurred in a crevice condition.
166
VIEW
ML00122 / Feb.2018
Crevice Corrosion in a Subsea System
M - Austenitic Stainless SteelP - CaseAp - Oil and GasCd - Crevice
Cm - Aspect Before AnalysisDf - Localized Corrosion
ML00065 — Erosion Corrosion of Monel PipingM - NiCu AlloyP - Seamless PipeAp - Chemical IndustryCd - Erosion Corrosion
Aspect of the piping cut in the longitudinal direction, presenting the leakage region close to the welded joint between the pipe and the 90° elbow. The original SCH 40 (3.7 mm thickness) presents an actual average thickness of 2 mm all through the piping extension, evidencing a general thinning. See the schematic drawing in the next figure.
364
VIEW
ML00065 / May.2017
Erosion Corrosion of Monel Piping
M - NiCu AlloyP - Seamless PipeAp - Chemical IndustryCd - Erosion Corrosion
Cm - Aspect Before AnalysisDf - Leakage