Aspect Before Analysis

2 cases · 2 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Application: Subsea Microstructure: Tempered Martensite Detail focus: Secondary Cracks clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Macroscopic detail of the stud, adjacent to the fracture, showing that there are several secondary cracks at the bottom of the thread fillets, without any deformation evidence. This reveals a brittle material behavior, although the hardness measured at the stud end revealed 33HRc, as should be expected by the material specification.
59
VIEW
ML00136 / Jun.2018
Hydrogen Cracks of Subsea Studs
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - Secondary Cracks
Aspect of the bolt surface with a detail of a secondary crack at the first thread fillet, close to the bolt head.
147
VIEW
ML00077 / Jun.2018
Hydrogen Cracking of LAS Subsea Bolts
M - Low Alloy Medium Carbon QTP - FastenerAp - SubseaCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - Secondary Cracks