Oil and Gas

2 cases · 25 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Pearlitic clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of the wire rope, 1 1/2" diameter, presenting regions of flattened areas at the surface of the outer wires. It is a 6 x 19 Seale construction, right regular lay.
552
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Aspect Before AnalysisDf - General View
The shaft was removed from service without a failure. It was 4' long and the diameters varied from 2 1/2" to 4 1/2". It was analyzed to be specified for purchasing a new one but properties evidenced bad ductility and brittle behavior even at ambient temperature, associated to a microestruture "as hot rolled".
1238
VIEW
ML00152 / Dec.2018
Low Alloy Steel Pump Shaft
M - High Strength Low AlloyP - ShaftAp - Oil and GasCd - Removed From Service
Cm - Aspect Before AnalysisDf - General View

More from these cases

ML00175 — Localized External Wear of a Wire RopeM - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Macrosection of the wire rope, transverse, showing 6 strands and an independent wire rope core (IWRC). Each strand presents three layers in a SEALE construction.
92
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Transverse Section AspectDf - Plastic Deformation
Low magnification micrography of a strain hardened pearlitic structure, in a longitudinal section, of one 3.2mm round wire of one strand.
62
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Highly strain hardened pearlitic structure of one external wire, 3.2mm diameter, of one strand.
55
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Nital Etched Micrography by OMDf - Pearlite
Micrographic detail of the strain hardened pearlitic structure, in a longitudinal section, of a 3.2mm external round wire of one strand. This structure presented a hardness level about 500 HV (1kg), measured in the center of the thickness in the metallographic section.
47
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Nital Etched Micrography by OMDf - Strain Hardened
Metallographic aspect of the wire surface in one strand external wire, showing the presence of oxides.
41
VIEW
ML00175 / Aug.2021
Localized External Wear of a Wire Rope
M - High Carbon SteelP - Wire RopeAp - Oil and GasCd - Wear
Cm - Nital Etched Micrography by OMDf - At the Surface

+11 more from this case →

ML00152 — Low Alloy Steel Pump ShaftM - High Strength Low AlloyP - ShaftAp - Oil and GasCd - Removed From Service
The longitudinal section of the shaft shows a coarse structure. Only very close to the surface the structure is slightly refined.
99
VIEW
ML00152 / Dec.2018
Low Alloy Steel Pump Shaft
M - High Strength Low AlloyP - ShaftAp - Oil and GasCd - Removed From Service
Cm - NItal Etched MacroDf - Longitudinal Section
The longitudinal section of the shaft, in the center of the thickness, shows a coarse structure, and a ferritic/bainitic structure with pearlite islands.
97
VIEW
ML00152 / Dec.2018
Low Alloy Steel Pump Shaft
M - High Strength Low AlloyP - ShaftAp - Oil and GasCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
The coarse structure in the center of the shaft thickness is evidenced by free ferrite islands at the previous austenite grains. The presence of a pearlitic structure evidences the slow cool of the material.
85
VIEW
ML00152 / Dec.2018
Low Alloy Steel Pump Shaft
M - High Strength Low AlloyP - ShaftAp - Oil and GasCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Coarse Structure
Micrographic detail of the pearlitic structure in the center of the shaft thickness.
82
VIEW
ML00152 / Dec.2018
Low Alloy Steel Pump Shaft
M - High Strength Low AlloyP - ShaftAp - Oil and GasCd - Removed From Service
Cm - Nital Etched Micrography by SEMDf - Pearlite
The longitudinal section of the shaft, at the surface, also shows a coarse structure, and a ferritic/bainitic structure with pearlite islands. There is only a small refining in the previous austenite grain boundaries, indicating that the material was not heat treated.
75
VIEW
ML00152 / Dec.2018
Low Alloy Steel Pump Shaft
M - High Strength Low AlloyP - ShaftAp - Oil and GasCd - Removed From Service
Cm - Nital Etched Micrography by OMDf - Longitudinal Section

+2 more from this case →