Offshore

2 cases · 37 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Product: Welded Joint Standard: ASTM clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Macrography of the welded joint upper part. Transverse section showing the different zones studied in this ML. See the schematic drawing in the next image.
454
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched MacroDf - Welded Joint
The repair weld presented several cracks in the weld metal, transverse to the weld, detected during inspection using magnetic particle test. The cracks were mainly located in regions of the structure where the repair was conducted by welding in the vertical position using 1/8" stick electrode.
710
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Aspect by NDTDf - Cracking

More from these cases

ML00045 — Subsea Tubular F6NM Martensitic SSM - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Schematic drawing presenting the different zones of the welded joint at the upper part.
49
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Identification drawingDf - Welded Joint
Macrography of the welded joint, at the root position, presenting the different zones studied in this ML. Transverse section. See the schematic drawing in the next image.
47
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched MacroDf - Welded Joint
Schematic drawing presenting the different zones of the welded joint
35
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Identification drawingDf - Welded Joint
Base metal micrographic detail presenting a tempered martensitic microstructure.
27
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched Micrography by OMDf - Base Metal
Micrographic detail of the heat-affected zone close to the base metal.
29
VIEW
ML00045 / Aug.2017
Subsea Tubular F6NM Martensitic SS
M - Martensitic Stainless SteelP - Fabrication WeldAp - OffshoreCd - Welding
Cm - Kalling Etched Micrography by OMDf - Heat Affected Zone

+15 more from this case →

ML00010 — Cold Cracks in a Gouged Weld MetalM - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
After grinding to remove the cracks, it was possible to see that they originated in the root, with longitudinal and transverse cracking, and localized in the weld metal only.
167
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Aspect by NDTDf - Cracking
Acetate metallographic replica from the surface, before cracking removal, showing the intergranular morphology of the cracks in a very refined weld metal structure.
123
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Nital etched, OMDf - Intergranular Cracking
Detail of the acetate metallographic replica from the surface, before cracking removal, showing the (previous austenite) intergranular morphology of the cracks in a very refined weld metal structure.
107
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Nital etched, OMDf - Intergranular Cracking
Tempered martensitic structure of the plate base metal.
93
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Base Metal
Detail of the tempered martensitic structure of the plate base metal. Hardness level of 27 HRc.
92
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Base Metal

+10 more from this case →