Offshore

2 cases · 9 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Detail focus: Corrosion clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
The threads of the carbon steel valve body is corroded. The offshore ambient is wet and chloride rich, creating an aggressive environment for the carbon steel threads.
99
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Surface AspectDf - Corrosion
Aspect of the hydraulic cylinder surface presenting white stains and black oxides in a region that started a localized dissolution under deposit.
72
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Aspect Before AnalysisDf - Corrosion

More from these cases

ML00184 — Dissimilar Steels in a Threaded ConnectionM - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Not only the threads were corroded but all regions under the painting that was detached from the surface.
86
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Surface AspectDf - Corrosion
Macrosection of the valve body at the thread, showing the position where the fitting was installed.
84
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Transverse Section AspectDf - Corrosion
ML00128 — MIC of a Stored Hydraulic CylinderM - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Detail of the cylinder external surface, with deep dissolution as the worst damage morphology.
65
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Aspect Before AnalysisDf - Corrosion
Micrographic aspect, after Nital etching, of the longitudinal section of the cylinder, at the surface, in a region where the damage is in the begining. There are two layers at the surface. A first Ni layer, 160 microns thick and 300HV average hardness, over the low carbon steel substrate, 200HV average hardness, and a chromium plated layer, 250 microns thick and 1100HV average hardness.
59
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Nital Etched Micrography by OMDf - Corrosion
Micrographic detail of the longitudinal section of the cylinder, at the surface, in a region where the Cr layer is detaching.
56
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Nital Etched Micrography by OMDf - Corrosion
Scanning electron microscopy image of the chromium plated cylinder in a region of localized dissolution under deposit. Inside the shallow pitting the Cr structure with a network of layers is revealed by the etching effect promoted by microbiollogically induced corrosion.
35
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Surface Aspect by SEMDf - Corrosion
Scanning electron microscopy image in detail of the chromium plated cylinder surface in a region of localized dissolution. The surface shows several microcracks promoted by the effects of the microbiollogically induced corrosion. Inside the corroded pit the network of the chromium layer is evidenced by the MIC attack.
48
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Surface Aspect by SEMDf - Corrosion