Offshore

2 cases · 25 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Damage Microstructure: Tempered Martensite clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the longitudinal section of the link, presenting secondary cracks in the longitudinal direction, following segregation bands in the material.
541
VIEW
ML00079 / Jul.2017
Hydrogen Cracking of a Maritime Chain Link
M - High Strength Low AlloyP - Chain LinkAp - OffshoreCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Secondary Cracks
The repair weld presented several cracks in the weld metal, transverse to the weld, detected during inspection using magnetic particle test. The cracks were mainly located in regions of the structure where the repair was conducted by welding in the vertical position using 1/8" stick electrode.
710
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Aspect by NDTDf - Cracking

More from these cases

ML00079 — Hydrogen Cracking of a Maritime Chain LinkM - High Strength Low AlloyP - Chain LinkAp - OffshoreCd - Hydrogen Embrittlement
Micrographic detail of the longitudinal section of the link, presenting internal cracks of intergranular morphology, typical of a hydrogen assisted mechanism.
52
VIEW
ML00079 / Jul.2017
Hydrogen Cracking of a Maritime Chain Link
M - High Strength Low AlloyP - Chain LinkAp - OffshoreCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Intergranular Cracking
Fracture appearance of the 1 1/4" diameter link. The fracture is flat and presented no evidences of plastic deformation, suggesting a brittle behavior.
54
VIEW
ML00079 / Jul.2017
Hydrogen Cracking of a Maritime Chain Link
M - High Strength Low AlloyP - Chain LinkAp - OffshoreCd - Hydrogen Embrittlement
Cm - Aspect Before AnalysisDf - General View
Micrography of a longitudinal section of the link, presenting a tempered martensitic structure, typical of a quenching and tempering heat treatment and compatible with the link hardness of 43 HRc.
67
VIEW
ML00079 / Jul.2017
Hydrogen Cracking of a Maritime Chain Link
M - High Strength Low AlloyP - Chain LinkAp - OffshoreCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Martensite
Macrography of the longitudinal section of the broken link, at the fracture surface. There are several secondary cracks, parallel and perpendicular to the link axis.
37
VIEW
ML00079 / Jul.2017
Hydrogen Cracking of a Maritime Chain Link
M - High Strength Low AlloyP - Chain LinkAp - OffshoreCd - Hydrogen Embrittlement
Cm - Longitudinal Section AspectDf - Longitudinal Section
Micrography of the longitudinal section of the link, close to the fracture surface (in the top of the figure). There are secondary cracks parallel to the fracture.
33
VIEW
ML00079 / Jul.2017
Hydrogen Cracking of a Maritime Chain Link
M - High Strength Low AlloyP - Chain LinkAp - OffshoreCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Secondary Cracks

+3 more from this case →

ML00010 — Cold Cracks in a Gouged Weld MetalM - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
After grinding to remove the cracks, it was possible to see that they originated in the root, with longitudinal and transverse cracking, and localized in the weld metal only.
167
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Aspect by NDTDf - Cracking
Acetate metallographic replica from the surface, before cracking removal, showing the intergranular morphology of the cracks in a very refined weld metal structure.
123
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Nital etched, OMDf - Intergranular Cracking
Detail of the acetate metallographic replica from the surface, before cracking removal, showing the (previous austenite) intergranular morphology of the cracks in a very refined weld metal structure.
107
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Nital etched, OMDf - Intergranular Cracking
Tempered martensitic structure of the plate base metal.
93
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Base Metal
Detail of the tempered martensitic structure of the plate base metal. Hardness level of 27 HRc.
92
VIEW
ML00010 / Oct.2017
Cold Cracks in a Gouged Weld Metal
M - Low Alloy Low Carbon QTP - Rolled PlateAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Base Metal

+10 more from this case →