Offshore

9 cases · 24 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Damage Detail focus: Microstructure clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrographic detail of the valve body carbon steel thread, in the valley. Ferritic-bainitic structure.
69
VIEW
ML00184 / Apr.2023
Dissimilar Steels in a Threaded Connection
M - Low Carbon SteelP - ForgingAp - OffshoreCd - Localized Dissolution
Cm - Nital Etched Micrography by OMDf - Bainitic Ferrite
Micrographic aspect of the longitudinal section of the cylinder steel substrate, presenting a ferritic-pearlitic structure.
207
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of the pin microstructure at the longitudinal section showing a tempered martensitic structure and a band of retained austenite.
61
VIEW
ML00085 / Nov.2017
Corrosion Fatigue of a Martensitic SS Pin
M - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Kalling Etched Micrography by OMDf - Martensite
Micrography of a longitudinal section of the link, presenting a tempered martensitic structure, typical of a quenching and tempering heat treatment and compatible with the link hardness of 43 HRc.
67
VIEW
ML00079 / Jul.2017
Hydrogen Cracking of a Maritime Chain Link
M - High Strength Low AlloyP - Chain LinkAp - OffshoreCd - Hydrogen Embrittlement
Cm - Nital Etched Micrography by OMDf - Martensite
Micrography of a longitudinal section of the pipe presenting a granular austenitic structure, typical of a solid solution annealing condition. No carbide precipitation.
62
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Micrography by OM using A262 Method ADf - Austenite
The micrography shows the martensitic region of the tube HAZ responsible for the hydrogen cracking, presenting too high hardness level (600 HV). It is a fresh martensite since the joint was welded in one pass and there was no PWHT.
45
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Martensite
Transverse section of the blade showing large grains of this poliycristaline cast material.
421
VIEW
ML00042 / Apr.2017
Gas Turbine Blade IN 939, Coated
M - NiCrCo AlloyP - CastAp - Gas TurbineCd - Intergranular Cracking
Cm - H2SO4+HNO3+H3PO4 Etched MicroDf - Coarse Structure
Regions of the localized corrosion spots associated to non metallic inclusions.
123
VIEW
ML00016 / Apr.2017
SCC in Free Cutting 303SS
M - Austenitic Stainless SteelP - Machined PartAp - OffshoreCd - Stress Corrosion
Cm - Surface Aspect by SEMDf - Non Metallic Inclusions

More from these cases

ML00128 — MIC of a Stored Hydraulic CylinderM - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Micrographic detail of the ferritic-pearlitic structure of the cylinder steel substrate.
41
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Nital Etched Micrography by OMDf - Ferrite and Pearlite
Micrography of the longitudinal section of the cylinder , at the surface, where it was not yet damaged. The steel substrate is in the bottom of the figure, the Ni layer is in the center and the Cr layer is in the top of the figure.
38
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Nital Etched Micrography by OMDf - Ni layer
Micrography of the interface between the steel substrate and the first Ni layer. The Ni layer, 160 microns thick and 300HV hardness, is uniform and presents no discontinuities.
37
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Nital Etched Micrography by OMDf - Ni layer
Micrography of the interface between the Ni layer (bottom) and the Cr layer (top of the figure). The Cr layer, 250 microns thick and 1100HV hardness, presents small pores and cracks (that appear like black shadows, not focused).
35
VIEW
ML00128 / Apr.2018
MIC of a Stored Hydraulic Cylinder
M - Low Carbon SteelP - Chromium PlatedAp - OffshoreCd - Localized Dissolution
Cm - Nital Etched Micrography by OMDf - Hard Chromium Layer
ML00085 — Corrosion Fatigue of a Martensitic SS PinM - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Micrographic detail of the pin microstructure at the longitudinal section showing a tempered martensitic structure and a band of retained austenite.
62
VIEW
ML00085 / Nov.2017
Corrosion Fatigue of a Martensitic SS Pin
M - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Kalling Etched Micrography by OMDf - Banded Structure
Micrographic detail of the pin microstructure at the longitudinal section showing a band of retained austenite in martensitic structure.
58
VIEW
ML00085 / Nov.2017
Corrosion Fatigue of a Martensitic SS Pin
M - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Kalling Etched Micrography by OMDf - Martensite
ML00052 — Cold Cracks in API 5CT L80 Tube Welded to a Structural PartM - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Micrography of the low alloy steel tube at the fusion line, presenting a martensitic structure at the HAZ and acicular ferrite in the weld metal.
41
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by OMDf - Fusion Line
Micrographic detail of the fusion line of the carbon steel plate, by scanning electron microscopy, showing the bainitic structure at the HAZ and ferritic structure in the weld metal.
34
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by SEMDf - Fusion Line
Micrographic detail of the fusion line of the low alloy steel tube, by scanning electron microscopy, showing the martensitic structure at the HAZ and acicular ferritic structure in the weld metal.
29
VIEW
ML00052 / Apr.2017
Cold Cracks in API 5CT L80 Tube Welded to a Structural Part
M - Low Alloy SteelP - Seamless tubeAp - OffshoreCd - Welding Defect
Cm - Nital Etched Micrography by SEMDf - Fusion Line
ML00042 — Gas Turbine Blade IN 939, CoatedM - NiCrCo AlloyP - CastAp - Gas TurbineCd - Intergranular Cracking
Micrography of the blade, view inside the grain. The intragranular precipitation presents one unique size of precipitation, not yet coalesced, although the blade was in high temperature service for 50.000 hours. Etched by H2SO4 + HNO3 + H3PO4 reagent.
66
VIEW
ML00042 / Apr.2017
Gas Turbine Blade IN 939, Coated
M - NiCrCo AlloyP - CastAp - Gas TurbineCd - Intergranular Cracking
Cm - Micrography by SEMDf - Intragranular Secondary Precipitation
ML00016 — SCC in Free Cutting 303SSM - Austenitic Stainless SteelP - Machined PartAp - OffshoreCd - Stress Corrosion
The pin microstructure in the longitudinal section shows austenitic structure, free from carbides, and sulfide inclusions that characterize the free cutting condition of this stainless steel.
77
VIEW
ML00016 / Apr.2017
SCC in Free Cutting 303SS
M - Austenitic Stainless SteelP - Machined PartAp - OffshoreCd - Stress Corrosion
Cm - Micrography by OM using A262 Method ADf - Non Metallic Inclusions