Offshore

2 cases · 15 images for “fatigue”

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Condition: Damage Capture method: Optical Microscope clear all

Results

SortRelevanceNewestOldestTitle A-ZTitle Z-A
Micrography of the pin microstructure at the longitudinal section showing a tempered martensitic structure and a band of retained austenite.
61
VIEW
ML00085 / Nov.2017
Corrosion Fatigue of a Martensitic SS Pin
M - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Kalling Etched Micrography by OMDf - Martensite
Micrography of a longitudinal section of the pipe (seamless), that shows the through wall cracking, straigth and not associated to any welded region or microstructural problem.
64
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Micrography by OM using A262 Method ADf - Through Wall Cracking

More from these cases

ML00085 — Corrosion Fatigue of a Martensitic SS PinM - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Micrographic detail of the pin microstructure at the longitudinal section showing a tempered martensitic structure and a band of retained austenite.
62
VIEW
ML00085 / Nov.2017
Corrosion Fatigue of a Martensitic SS Pin
M - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Kalling Etched Micrography by OMDf - Banded Structure
Micrographic detail of the pin microstructure at the longitudinal section showing a band of retained austenite in martensitic structure.
58
VIEW
ML00085 / Nov.2017
Corrosion Fatigue of a Martensitic SS Pin
M - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Kalling Etched Micrography by OMDf - Martensite
Micrography of the pin in a longitudinal section, transverse to the fracture surface, close to the point of cracking iniciation, presenting a flat propagation and a secondary crack, paralel to the fracture surface.
54
VIEW
ML00085 / Nov.2017
Corrosion Fatigue of a Martensitic SS Pin
M - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Kalling Etched Micrography by OMDf - Fracture
Micrography of the pin in a longitudinal section, transverse to the fracture surface, close to the point of cracking iniciation, presenting a flat propagation and a secondary crack, paralel to the fracture surface.
52
VIEW
ML00085 / Nov.2017
Corrosion Fatigue of a Martensitic SS Pin
M - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Kalling Etched Micrography by OMDf - Fracture
Micrographic detail of a secondary cracking close to the fracture position. The crack presents no plastic deformation, is slightly branched and filled with products.
52
VIEW
ML00085 / Nov.2017
Corrosion Fatigue of a Martensitic SS Pin
M - Martensitic Stainless SteelP - Forged PinAp - O&G Well DrillingCd - Corrosion Fatigue
Cm - Kalling Etched Micrography by OMDf - Fatigue Fracture

+6 more from this case →

ML00012 — Vibration Induced Fatigue in a 316/316L SSM - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Micrography of the pipe in a longitudinal section, close to the external surface, showing a pit (adjacent to the through wall cracking). The corrosion spt is not associated to any microstructural feature.
61
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Micrography by OMDf - Pitting
Micrography of a longitudinal section of the pipe presenting a granular austenitic structure, typical of a solid solution annealing condition. No carbide precipitation.
62
VIEW
ML00012 / Aug.2017
Vibration Induced Fatigue in a 316/316L SS
M - Austenitic Stainless SteelP - Seamless PipeAp - OffshoreCd - Vibration Induced Fatigue
Cm - Micrography by OM using A262 Method ADf - Austenite