Crevice Corrosion in a Subsea System — Aspect Before Analysis

Standard: AISI Capture method: Nital Etched Micrography by OM clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Low magnification micrography presenting segregation bands in a martensitic structure. In the segregated regions the Nital etch effect is lower and the bands appear lighter. The black spots and lines are inclusions (some elongated) in the band.
91
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Longitudinal Section
Micrography of an axial section of the roller bearing, at the external surface, where the hardness level was about 64 HRc (higher than the limit of 58HRc to 62 HRc).
86
VIEW
ML00131 / Apr.2018
Brittle Failure of a Soft Roller Bearing
M - Wear Resistant SteelP - Roller BearingAp - Mechanical IndustryCd - Heat Treatment Defect
Cm - Nital Etched Micrography by OMDf - Close to the External Surface

More from these cases

ML00182 — Brittle Fracture of a LAS Fixing RodM - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Micrography presenting segregation bands (less etched) in a tempered martensitic microstructure.
81
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Segregated Regions
Micrography presenting a tempered martensitic microstructure, with light etch in segregated bands.
74
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Tempered Martensite
Micrography perpendicular to the fracture surface showing, in the secondary cracks, the intergranular morphology of the fracture.
33
VIEW
ML00182 / Jul.2022
Brittle Fracture of a LAS Fixing Rod
M - Low Alloy Medium Carbon QTP - StemAp - Mechanical IndustryCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Intergranular Cracking
ML00131 — Brittle Failure of a Soft Roller BearingM - Wear Resistant SteelP - Roller BearingAp - Mechanical IndustryCd - Heat Treatment Defect
Micrographic detail of the roller bearing microstructure, close to the external surface, presenting 64 HRc and a microstructure that is martensitic with large carbides.
86
VIEW
ML00131 / Apr.2018
Brittle Failure of a Soft Roller Bearing
M - Wear Resistant SteelP - Roller BearingAp - Mechanical IndustryCd - Heat Treatment Defect
Cm - Nital Etched Micrography by OMDf - Martensite
Micrographic detail of the roller bearing microstructure, close to the external surface, presenting 64 HRc and a microstructure that is martensitic with large carbides, several presenting internal cracks.
82
VIEW
ML00131 / Apr.2018
Brittle Failure of a Soft Roller Bearing
M - Wear Resistant SteelP - Roller BearingAp - Mechanical IndustryCd - Heat Treatment Defect
Cm - Nital Etched Micrography by OMDf - Cracks
Micrography of an axial section of the roller bearing, at the internal surface, where the hardness level was about 21 HRc, indicating that in this region the material was not properly quenched and tempered.
75
VIEW
ML00131 / Apr.2018
Brittle Failure of a Soft Roller Bearing
M - Wear Resistant SteelP - Roller BearingAp - Mechanical IndustryCd - Heat Treatment Defect
Cm - Nital Etched Micrography by OMDf - Close to the Internal Surface
Micrographic detail of the roller bearing microstructure, close to the internal surface, presenting 21 HRc that reveals that the matrix is not martensitic. It is ferritic with large aligned carbides (cracked).
72
VIEW
ML00131 / Apr.2018
Brittle Failure of a Soft Roller Bearing
M - Wear Resistant SteelP - Roller BearingAp - Mechanical IndustryCd - Heat Treatment Defect
Cm - Nital Etched Micrography by OMDf - Ferrite
Micrographic detail of the roller bearing microstructure, close to the internal surface, presenting 21 HRc and a microstructure that is ferritic with large carbides (cracked) and small round carbides.
63
VIEW
ML00131 / Apr.2018
Brittle Failure of a Soft Roller Bearing
M - Wear Resistant SteelP - Roller BearingAp - Mechanical IndustryCd - Heat Treatment Defect
Cm - Nital Etched Micrography by OMDf - Cracks

+5 more from this case →