Lifting

2 cases · 39 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Tempered Martensite clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Aspect of the barrel nut that is broken in a brittle way (without plastic deformation). The Nut diameter is 1", the nut length is 2" and the bolt thread is 1/2" (nominal diameter).
753
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Aspect Before AnalysisDf - General View
Micrography of a transverse section of the lifting part, showing interdendritic voids close to the surface at the inner diameter of the padeye. The microstructure is tempered martensite.
450
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Casting defects

More from these cases

ML00148 — Brittle Fracture of a 420 SS Barrel NutM - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Visual aspect of both sides of the fractures. They present a macroscopically brittle aspect, with chevron marks indicating the starting point at the thinner edge of the thread.
81
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Aspect Before AnalysisDf - Fracture
The fracture is flat, in the region of the lower resistant section, presenting no macroscopic evidences of plastic deformation. The starting point of the fracture is indicated by the chevron marks.
62
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Fracture Surface AspectDf - Chevron Marks
Low magnification micrography of the nut in the longitudinal section, presenting the machined internal thread and a banded microstructure.
55
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Banded Structure
Microstructural aspect of a longitudinal section of the nut, in the middle of the thickness. Martensitic structure, banded.
46
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Banded Structure
Microstructural detail of the banded structure. The rough aspect of the band is created by the carbides (better seen in the higher magnification image) in the segregation band.
38
VIEW
ML00148 / Sep.2018
Brittle Fracture of a 420 SS Barrel Nut
M - Martensitic Stainless SteelP - Barrel NutAp - LiftingCd - Heat Treatment Defect
Cm - Kalling Etched Micrography by OMDf - Banded Structure

+15 more from this case →

ML00098 — Brittle Fracture of a Casting Lifting DeviceM - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Aspect of the broken padeye. The outer diameter is about 10" and the thickness of the casting is about 2".
22
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - General View
Aspect of the fracture surface, showing a brittle morphology. Flat fracture with chevron marks from regions close to the internal diameter of the padeye, where there are secondary cracks.
22
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Aspect Before AnalysisDf - Fracture
Micrography of the lifting padeye showing a dendritic path of a quenched and tempered martensitic microstructure. The segregated regions (white interdendritic regions) are more clearly identified in low magnification. Voids are located in these segregated regions.
21
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Martensite
Micrography of the lifting padeye showing a quenched and tempered martensitic microstructure. Voids are located in interdendritic segregated regions.
20
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Martensite
Micrography of the lifting padeye showing a quenched and tempered martensitic microstructure. Voids are located in interdendritic segregated regions. At this magnification the segregation is not clear.
16
VIEW
ML00098 / Nov.2017
Brittle Fracture of a Casting Lifting Device
M - Low Alloy Medium Carbon QTP - CastingAp - LiftingCd - Brittle Fracture
Cm - Nital Etched Micrography by OMDf - Martensite

+12 more from this case →