FPSO

2 cases · 12 images

Crevice Corrosion in a Subsea System — Aspect Before Analysis

Microstructure: Duplex Ferritic Austenitic Detail focus: Heat Affected Zone clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Micrography of the heat affected zone of the pipe to the fitting, at the pipe position, where the weld is in angle to the pipe (welded at the pipe surface). Weld metal to the top.
85
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - NaOH Electrolytic Etched MicroDf - Heat Affected Zone
Macrography of the pipe heat affected zone.
55
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MacroDf - Heat Affected Zone

More from these cases

ML00150 — Vibration Induced Fatigue in a SS Oil PipingM - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Micrography of the heat affected zone of the pipe to the fitting, at the pipe position. Base metal to the bottom of the figure and fusion line to the top.
87
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - NaOH Electrolytic Etched MicroDf - Heat Affected Zone
Micrography of the heat affected zone (HAZ) of the pipe. The amount of ferrite in the HAZ is a little higher than in the pipe base metal.
86
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - NaOH Electrolytic Etched MicroDf - Heat Affected Zone
Micrography of the heat affected zone of the pipe to the fitting, at the fitting position. The fitting is welded in the thickness. The fusion line is in the bottom of the figure.
74
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - NaOH Electrolytic Etched MicroDf - Heat Affected Zone
Micrography of the heat affected zone (HAZ) of the fitting, welded to the pipe. The forged fitting base metal is to the top of the figure and the fusion line is to the bottom.
71
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - NaOH Electrolytic Etched MicroDf - Heat Affected Zone
Micrography of the heat affected zone (HAZ) of the fitting. The amount of ferrite in the HAZ is a little higher than in the pipe base metal.
70
VIEW
ML00150 / Dec.2018
Vibration Induced Fatigue in a SS Oil Piping
M - Duplex Stainless SteelP - PipingAp - FPSOCd - Vibration Induced Fatigue
Cm - NaOH Electrolytic Etched MicroDf - Heat Affected Zone
ML00049 — Pipe to Flange Welded Joint in a 14" ND Superduplex SpoolM - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Macrography of the flange HAZ. The macroscopic aspect shows a remarkable modified region.
56
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MacroDf - Heat Affected Zone
Micrography of the pipe heat affected zone. In the left the pipe base metal, with banded duplex structure; and in the right the weld metal, with Widmanstatten morphology of the structure.
43
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MicroDf - Heat Affected Zone
Higher magnification of the pipe heat affected zone. The amount of ferrite increases with the proximity of the fusion line (to the right).
38
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MicroDf - Heat Affected Zone
Micrography of the flange heat affected zone. In the right the flange base metal, with coarse structure and detrimental phases associated to the ferrite; and in the left the weld metal, with Widmanstatten morphology of the structure.
36
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MicroDf - Heat Affected Zone
Higher magnification of the flange heat affected zone. The detrimental phases in the ferrite structure is clearly being dissolved with the proximity of the fusion line (to the left).
28
VIEW
ML00049 / Apr.2017
Pipe to Flange Welded Joint in a 14" ND Superduplex Spool
M - Super Duplex Stainless SteelP - Piping spoolAp - Oil and GasCd - Removed From Service
Cm - NaOH Electrolytic Etched MicroDf - Heat Affected Zone