Crevice Corrosion in a Subsea System — Aspect Before Analysis

Detail focus: Cracking clear all

Results

SortNewestOldestTitle A-ZTitle Z-A
Gas piping. Aspect of a branching line 2" ND, lateral to a horizontal main pipe ND 8", welded using a weldolet. The cracking started at the margin of the weld in the upper part of the pipe, where the weld crossed the longitudinal direction of the pipe, perpendicular to the branch.
932
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect Before AnalysisDf - Cracking
Aspect of the heat exchanger plate showing the rupture of the plate in multiple cracks, starting at the side of the crude oil with high salinity.
727
VIEW
ML00051 / Apr.2020
Chloride SCC of 316 Heat Exchanger Plate
M - Austenitic Stainless SteelP - Heat Exchanger PartAp - FPSOCd - Stress Corrosion
Cm - Aspect Before AnalysisDf - Cracking

More from these cases

ML00149 — Vibration Induced Fatigue in a Gas PipingM - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Aspect by dye check of the upper side of the pipe, at the margin of the weld between the main pipe and the lateral branch, presenting a fatigue cracking initiated at the external side, probably induced by vibration.
68
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Aspect by NDTDf - Cracking
Macrography of the 8" pipe, welded to a 2" fitting (weldolet), welded to a 2" flange. The branch line was operating in this position (horizontal line with a lateral branch) and the through thickness fatigue crack is associated to the margin of the weld in the upper part of the pipe.
50
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - NItal Etched MacroDf - Cracking
Micrography of a section tranverse to the pipe and to the weld between the 8"pipe and the 2" fitting weldolet. The crack starts exactly at the margin of the weld and propagates in the pipe longitudinal direction, in a straight line, not related to any metallurgical aspect.
30
VIEW
ML00149 / Dec.2018
Vibration Induced Fatigue in a Gas Piping
M - Low Carbon SteelP - Piping spoolAp - FPSOCd - Vibration Induced Fatigue
Cm - Micrography by OMDf - Cracking
ML00051 — Chloride SCC of 316 Heat Exchanger PlateM - Austenitic Stainless SteelP - Heat Exchanger PartAp - FPSOCd - Stress Corrosion
Macrography of the surface of the cracked heat exchanger plate, manufactured in austenitic stainless steel.
159
VIEW
ML00051 / Apr.2020
Chloride SCC of 316 Heat Exchanger Plate
M - Austenitic Stainless SteelP - Heat Exchanger PartAp - FPSOCd - Stress Corrosion
Cm - Macro Oxalic Acid Electrolytic EtchedDf - Cracking