Micrography of a crankshaft longitudinal section at the shaft edge, in the as polished condition, presenting nodular graphite, well distruibuted.
139
VIEW
ML00154 / Jan.2019
High Strength Cast Iron Crankshaft
M - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Cm - As polished micrographyDf - At the Surface
Micrography as polished of the longitudinal section of the bolt at the fracture position. The fracture (top of the figure) is rough, characteristic of a ductile fracture.
196
VIEW
ML00120 / Jun.2018
Ductile Rupture of a Carbon Steel Eye Bolt
M - Low Carbon SteelP - FastenerAp - AutomotiveCd - Overload
Cm - As polished micrographyDf - Fracture

More from these cases

ML00154 — High Strength Cast Iron CrankshaftM - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
As polished micrography of the crankshaft at the shaft edge, close to the surface. Graphite in nodules.
126
VIEW
ML00154 / Jan.2019
High Strength Cast Iron Crankshaft
M - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Cm - As polished micrographyDf - Graphite in Nodules
As polished micrographic detail of the graphite in nodules, close to the surface of the shaft edge, in a longitudinal section.
114
VIEW
ML00154 / Jan.2019
High Strength Cast Iron Crankshaft
M - Nodular Cast IronP - CastingAp - EngineCd - Surface treatment
Cm - As polished micrographyDf - Graphite in Nodules